@article { ISI:000288483400033, title = {Characterization of surface acid sites in tin-silicalite-1 (Sn-MFI) molecular sieve by X-ray photoelectron spectroscopy}, journal = {Microporous and Mesoporous Materials}, volume = {141}, number = {1-3}, year = {2011}, month = {MAY}, pages = {236-240}, publisher = {ELSEVIER SCIENCE BV}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

The nature, strength and density of surface acid sites in Sn-MFI molecular sieves with different Sn-content were characterized by N 1s high resolution photoelectron peak of chemisorbed pyridine in combination with pyridine-IR and TPAD. Two peaks emerged at 399.5 +/- 0.2 and 401.5 +/- 0.2 eV by deconvoluting composite N is peak were assigned to chemisorbed pyridine on weak and relatively strong Lewis acid sites, respectively. The relative percentage of strong Lewis acid sites was found to increase with the decrease of framework Sn content. A close agreement was observed between the ratios of weak Lewis acid sites to strong Lewis acid sites obtained from XPS and TPAD. (C) 2010 Elsevier Inc. All rights reserved.

}, keywords = {Lewis acidity, Pyridine chemisorption, SiO2/SnO2 molar ratio, Sn-MFI, XPS}, issn = {1387-1811}, doi = {10.1016/j.micromeso.2010.10.036}, author = {Niphadkar, P. S. and Patil, K. R. and Joshi, P. N.} } @article { ISI:000306358100005, title = {Copper modified waste fly ash as a promising catalyst for glycerol hydrogenolysis}, journal = {Catalysis Today}, volume = {190}, number = {1}, year = {2012}, month = {AUG}, pages = {31-37}, publisher = {ELSEVIER SCIENCE BV}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

Several catalyst formulations using waste fly ash along with Cu were prepared and characterised by XRD, BET and TEM. These catalysts were also evaluated for the first time for hydrogenolysis of glycerol to 1,2 propanediol (1,2-PDO) in a batch reactor under 52 bar H-2 pressure in the temperature range of 473-513 K conditions. The fly ash pretreated by alkali using the fusion method and impregnated with Cu showed higher activity and stability for glycerol hydrogenolysis. Due to pretreatment with alkali at high temperature, transformation of alpha-quartz to the tridymite phase of SiO2 occurred. More importantly, use of alkali either during the pretreatment or the Cu loading step resulted in a high dispersion on the surface which was responsible for higher glycerol conversion and 1,2-PDO selectivity. The effects of temperature, Cu loading and solvent on glycerol conversion and product selectivities were also studied in this work. (C) 2011 Elsevier B.V. All rights reserved.

}, keywords = {1, 2-Propanediol, Alkali fusion, Cu loading, Fly ash, Glycerol hydrogenolysis}, issn = {0920-5861}, doi = {10.1016/j.cattod.2011.11.038}, author = {Rode, C. V. and Mane, R. B. and Potdar, A. S. and Patil, P. B. and Niphadkar, P. S. and Joshi, P. N.} } @article { ISI:000326058500009, title = {Crystallization kinetics of Sn-MFI molecular sieve formation by dry gel cross mark conversion method}, journal = {Microporous and Mesoporous Materials}, volume = {182}, year = {2013}, month = {DEC}, pages = {73-80}, publisher = {ELSEVIER SCIENCE BV}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

The conversion of amorphous stannosilicate dry gel into crystalline molecular sieve with MFI structure (Sn-MFI) was achieved by dry gel conversion (DGC) method at 413, 443 and 473 K. For comparison purpose, Sn-MFI molecular sieve with similar SiO2/SnO2 mole ratio was also obtained by hydrothermal crystallization route. Crystallization curves were established by conducting time dependant studies on progressive crystallization processes for both the systems. The values of activation energy of nucleation (E-n), activation energy of crystallization (E-c), and their pre-exponential factors (InA(n), InA(c) respectively) were calculated from Arrhenius plots. Compared to the hydrothermal method, shorter induction period was observed when DGC method was employed. Both the E-n (49.70 kJ/mol) and E-c (52.82 kJ/mol) for DGC method were found to be lower than that of the E-n (55.70 kJ/mop and E-c (60.23 kJ/mol) for hydrothermal method. The kinetics parameters viz. K and q were derived from kinetic expressions and DGC method showed higher value of K and lower value of q compared to hydrothermal crystallization method at identical temperature. Various DGC method parameters such as water content at the bottom of autoclave and SiO2/SnO2 mole ratio have shown the influence on the kinetics of crystallization of Sn-MFI. (C) 2013 Elsevier Inc. All rights reserved.

}, keywords = {Crystallization, DGC, kinetics, Nucleation, Sn-MFI}, issn = {1387-1811}, doi = {10.1016/j.micromeso.2013.08.026}, author = {Niphadkar, P. S. and Tangale, N. P. and Joshi, P. N. and Awate, S. V.} }