	title = {Synthesis and characterization aromatic copolyesters bearing pendant norbornenyl groups},
	journal = {High Performance Polymers},
	volume = {38},
	year = {2026},
	month = {MAY},
	pages = {254-263},
	type = {Article},
	abstract = {<p>
	4, 4{\textquoteright}-(Bicyclo (2.2.1) hept-5-en-2 yl methylene) bis (2-methoxyphenol) (BPA-NB) was polymerized via phase transfer catalyzed interfacial polycondensation with an equimolar mixture (50:50 mol \%) of isophthaloyl chloride (IPC) and terephthaloyl chloride (TPC) to obtain aromatic copolyester bearing pendant norbornenyl groups (PES-NB). Furthermore, three different compositions of BPA-NB and bisphenol A (BPA) were polycondensed with IPC to obtain a series of copolyesters. 1H NMR spectroscopy confirmed the chemical structure and compositions of PES-NBs. Inherent viscosity and number-average molecular weight values of PES-NBs were in the range 0.82 to 1.06 dLg-1 and 63,600 to 95,300 gmol-1, respectively, indicating the formation of polymers of reasonably high molecular weights. PES-NBs readily dissolved in common organic solvents such as chloroform, dichloromethane, and tetrahydrofuran, and tough, transparent, flexible films could be cast from their chloroform solutions. X-Ray diffraction studies indicated amorphous nature of PES-NBs. Glass transition temperature (Tg) values of PES-NBs were in the range 215 to 195 degrees C and Tg values increased with the increase in mol \% of BPA-NB.</p>
},
	keywords = {aromatic (co)polyesters, glass-transition temperature (Tg), interfacial polycondensation, norbornenyl groups},
	issn = {0954-0083},
	doi = {10.1177/09540083251415177},
	author = {Talanikar, Aniket A. and Bhong, Sahil T. and Nagane, Samadhan S. and Wadgaonkar, Prakash P. and Rashinkar, Gajanan S.}
}