	title = {Sulfonated polyvinyl alcohol ionomer membrane favoring smooth electrodeposition of zinc for aqueous rechargeable zinc metal batteries},
	journal = {Sustainable Energy \& Fuels},
	volume = {5},
	year = {2021},
	month = {OCT},
	pages = {5557-5564},
	type = {Article},
	abstract = {One of the failure mechanisms of aqueous rechargeable zinc metal batteries (AZMBs) involves high surface area zinc (HSAZ)/dendrite-like deposits over the Zn-metal anode during long-term cycling. Negatively charged (anionic) polymeric ionomer electrolyte membranes and separators are known for suppressing the dendrite-/HSAZ-induced failure of AZMBs. However, the preparation of cost-effective and non-fluorinated ionomers from cheap and environmentally friendly polymers is essential to leverage the feasibility of AZMBs. The current work demonstrates the potential of an ionomer electrolyte membrane (P-AS-C-Zn) made by the crystallization-induced physical cross-linking of sulfonated poly (vinyl alcohol) (PVS) and poly (vinyl alcohol) (PVA) as a dendrite-/HSAZ-inhibiting separator for AZMBs. The P-AS-C-Zn membranes exhibited excellent Zn plating/stripping behavior with a stable voltage vs. time profile beyond 1100 h, compared to their neutral PVA-C-Zn counterpart without any ionomer character (cell failure at close to 280 h). Applying the optimized P-AS-C-Zn membrane in a MnO2||Zn full cell helps retain about 50\% of the initial capacity close to 600 cycles in the absence of extra manganese salt in the electrolyte, which is indeed promising.},
	issn = {2398-4902},
	doi = {10.1039/d1se00865j},
	author = {Vijayakumar, Vidyanand and Torris, Arun and Kurian, Maria and Mathew, Megha Mary and Ghosh, Meena and Khairnar, Ajay B. and Badiger, Manohar V. and Kurungot, Sreekumar}
}