@article { ISI:000274269700021,
	title = {Effect of reduced particle size on the magnetic properties of chemically synthesized BiFeO3 nanocrystals},
	journal = {Journal of Physical Chemistry C},
	volume = {114},
	number = {5},
	year = {2010},
	month = {FEB},
	pages = {2108-2115},
	publisher = {AMER CHEMICAL SOC},
	address = {1155 16TH ST, NW, WASHINGTON, DC 20036 USA},
	abstract = {<p>Here, we report the effect of reduction in particle size on the temperature dependent magnetization of chemically synthesized BiFeO3 nanocrystals with average grain size of 55 nm. The X-ray photoelectron spectroscopy results show a significant broadening of binding energy peaks associated to Fe3+ 2p(3/2) core levels due to the reduced size. Additionally, due to the nanosize effect, the M-H loops show a significant coercivity starting from 390 K with an anomaly located in the vicinity of 150 K in our H-c vs T as well as M-r/M-s(50 kOe) vs T curves. At this temperature, both H-c and M-r/M-s(50 kOe) undergo minima. Additionally, our results for the first time show the evidence of existence of a low temperature anomaly due to spin-glass transition in the range from 40-44 K in the field cooled magnetization curves. In bulk single crystals, this transition is reported to be situated at around 50 K, however, this transition remained so far undiscovered in the recent studies on BiFeO3 nanoparticles due to the insufficient temperature resolution. The significant shift in this transition toward lower temperature can be attributed to size dependent effects. Our results clearly present new information on the size dependent properties of BiFeO3 nanoparticles.</p>},
	issn = {1932-7447},
	doi = {10.1021/jp910745g},
	author = {Jaiswal, Adhish and Das, Raja and Vivekanand, K. and Abraham, Priya Mary and Adyanthaya, Suguna D. and Poddar, Pankaj}
}
@article { ISI:000289149900115,
	title = {Effect of particle size and annealing on spin and phonon behavior in TbMnO3},
	journal = {Journal of Applied Physics},
	volume = {109},
	number = {6},
	year = {2011},
	month = {MAR},
	pages = {064309},
	publisher = {AMER INST PHYSICS},
	address = {CIRCULATION \& FULFILLMENT DIV, 2 HUNTINGTON QUADRANGLE, STE 1 N O 1, MELVILLE, NY 11747-4501 USA},
	abstract = {<p>Interest has grown to study TbMnO3 as it was recently reported to show a gigantic magnetoelectric effect. Here, we report the synthesis and detailed magnetic and Raman spectroscopy study on TbMnO3 particles of size similar to 25 nm and 2-3 mu m, respectively. The incommensurate-commensurate (lock-in) transition, usually observed at 27 K for bulk phase of TbMnO3 was not observed in susceptibility versus T curve but was seen at 30 K in the coercivity versus T curve in similar to 25 nm particles. This transition, which is due to the spin modulation length scale, gets weakened in nanosize due to the increased intrinsic lattice strain observed in 2-3 mu m particles, due to the effect of increased particle size. The increased value of magnetization in the 2-3 mu m sample was attributed to double exchange interactions between Mn+3 and Mn+4 spins. The role of annealing related effects on the fate of the Neel temperature for TbMnO3 was investigated. Raman spectroscopy indicated a decrease in the lattice distortion for similar to 25 nm particles. (c) 2011 American Institute of Physics. [doi:10.1063/1.3563571]</p>},
	issn = {0021-8979},
	doi = {10.1063/1.3563571},
	author = {Das, Raja and Jaiswal, Adhish and Adyanthaya, Suguna D. and Poddar, Pankaj}
}