@article {46072,
	title = {Aromatic polyesters containing pendant azido groups: synthesis, characterization, chemical modification and thermal cross-linking},
	journal = {European Polymer Journal},
	volume = {116},
	year = {2019},
	month = {JUL},
	pages = {180-189},
	type = {Article},
	abstract = {<p>A partially bio-based bisphenol containing pendant azido group viz., 4,4{\textquoteright}-(5-azidopentane-2,2-diyl) diphenol (AZBPA) was synthesized starting from 4,4{\textquoteright}-bis (4-hydroxyphenyl) pentanoic acid. AZBPA was reacted with isophthaloyl chloride (IPC), terephthaloyl chloride (TPC) and a mixture of IPC/TPC (50:50 mol\%) by phase transfer-catalyzed interfacial polycondensation route to obtain aromatic polyesters containing pendant azido groups. Copolyesters containing pendant azido groups were also synthesized by polycondensation of different molar proportions of AZBPA and commercially available 4,4{\textquoteright}-(1-phenylethane-1,1-diyl) diphenol (BPA-AP) with IPC. Inherent viscosities and number average molecular weights of (co)polyesters were in the range 0.85-1.64 dL/g and 58,900-190,400, respectively, indicating the formation of reasonably high molecular weight polymers. Tough, transparent, and flexible films could be cast from chloroform solutions of these polyesters. X-Ray diffraction analysis showed that (co)polyesters were amorphous in nature. (Co)polyesters were characterized using FT-IR, H-1 NMR spectroscopy, XRD, TGA and DSC analysis. The chemical modification of a representative copolyester containing pendant azido groups was carried out quantitatively using copper-catalyzed azide-alkyne cycloaddition (CuAAC) with two alkynes viz., phenyl acetylene (PA) and ethynyl-4-nitrobenzene (ENB). Additionally, (co)polyesters containing pendant azido groups were thermally cross-linked (170 degrees C/12 h) leading to the formation of network structures based on azide to nitrene decomposition and subsequent reactions on polyester backbone. The selected cross-linked polyesters were characterized by stress-strain measurements. The cross-linked polymers exhibited higher tensile strength and Young{\textquoteright}s modulus and lower \% elongation at break compared to corresponding pristine polyesters containing pendant azido groups.</p>
},
	keywords = {Aromatic polyester, Chemical modification, Click chemistry, Pendant azido group, Thermal cross-linking},
	issn = {0014-3057},
	doi = {10.1016/j.eurpolymj.2019.04.019},
	author = {Nagane, Samadhan S. and Verma, Savita and Tawade, V, Bhausaheb and Sane, Prakash S. and Dhanmane, Sushilkumar A. and Wadgaonkar, Prakash P.}
}
@article {45483,
	title = {Design and synthesis of aromatic polyesters bearing pendant clickable maleimide groups},
	journal = {Journal of Polymer Science Part A-Polymer Chemistry},
	volume = {57},
	year = {2019},
	month = {MAR },
	pages = {630-640},
	type = {Article},
	abstract = {<p>A bisphenol bearing pendant maleimide group, namely, N-maleimidoethyl-3, 3-bis(4-hydroxyphenyl)-1-isobenzopyrrolidone (PPH-MA) was synthesized starting from phenolphthalein. Aromatic (co)polyesters bearing pendant maleimide groups were synthesized from PPH-MA and aromatic diacid chlorides, namely, isophthaloyl chloride (IPC), terephthaloyl chloride (TPC), and 50:50 mol \% mixture of IPC and TPC by low temperature solution polycondensation technique. Copolyesters were also synthesized by polycondensation of different molar proportions of PPH-MA and bisphenol A with IPC. Inherent viscosities and number-average molecular weights of aromatic (co)polyesters were in the range of 0.52-0.97 dL/g and 20,200-32,800 g/mol, respectively indicating formation of medium to reasonably high-molecular-weight polymers. C-13 NMR spectral analysis of copolyesters revealed the formation of random copolymers. The 10\% weight loss temperature of (co)polyesters was found in the range 470-484 degrees C, indicating their good thermal stability. A selected aromatic polyester bearing pendant maleimide groups was chemically modified via thiol-maleimide Michael addition reaction with two representative thiol compounds, namely, 4-chlorothiophenol and 1-adamantanethiol to yield post-modified polymers in a quantitative manner. Additionally, it was demonstrated that polyester containing pendant maleimide groups could be used to form insoluble crosslinked gel in the presence of a multifunctional thiol crosslinker. (c) 2018 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2019, 57, 630-640</p>},
	keywords = {crosslinking, maleimide group, modification, polyesters, thiol-maleimide},
	issn = {0887-624X},
	doi = {10.1002/pola.29303},
	author = {Nagane, Samadhan S. and Kuhire, Sachin S. and Jadhav, Uday A. and Dhanmane, Sushilkumar A. and Wadgaonkar, Prakash P.}
}