@article {44042, title = {Nutty carbon: morphology replicating hard carbon from walnut shell for na ion battery anode}, journal = {ACS Omega}, volume = {2}, year = {2017}, month = {JUL}, chapter = {3601{\textendash}3609}, abstract = {
Abstract Image

Efficient Na ion intercalation/deintercalation in the semigraphitic lattice of a hard carbon derived from the walnut shell is demonstrated. High-temperature (1000 {\textdegree}C) pyrolysis of walnut shells under an inert atmosphere yields a hard carbon with a low surface area (59 m2\ g{\textendash}1) and a large interplanar\ c\ axis separation of 0.39{\textendash}0.36 nm as compared to 0.32 nm for graphite, suitable for Na ion intercalation/deintercalation. A stable reversible capacity of 257 mAh g{\textendash}1\ is observed at a current density of 50 mA g{\textendash}1\ for such nutshell-derived carbon (NDC) with an impressive rate performance. No loss of electrochemical performance is observed for high current cycling (100 mA g{\textendash}1\ {\textrightarrow} 2 A g{\textendash}1\ {\textrightarrow} 100 mA g{\textendash}1). Additionally, the NDC shows remarkably stable electrochemical performance up to 300 charge{\textendash}discharge cycles at 100 mA g{\textendash}1\ with a minimal drop in capacity.

}, keywords = {Batteries, Biological and Medicinal chemistry, Biological materials, diffraction, Electric Properties, Electrode-electrolyte interface, spectra, Surface structure, Thermal properties}, doi = {10.1021/acsomega.7b00633}, author = {Wahid, M. and Gawli, Y. and Puthusseri, D. and Kumar, A. and Shelke, M. V. and Ogale, S.} }