@article {45418,
	title = {Spiro [fluorene-9,9 {\textquoteright}-xanthene]-containing copolymers of intrinsic microporosity: synthesis, characterization and gas permeation properties},
	journal = {Reactive \& Functional Polymers},
	volume = {133},
	year = {2018},
	month = {2018},
	pages = {153-160},
	type = {Article},
	abstract = {In the present study, a new bis(catechol) containing spiro[fluorene-9,9{\textquoteright}-xanthene], namely, 4,4{\textquoteright}-(spiro(fluorene9,9{\textquoteright}-xanthene]-2{\textquoteright},7{\textquoteright}-diyl)bis(benzene-1,2-diol) (THSFX) was designed and synthesized. Polycondensation reactions of THSFX and varying compositions of THSFX and 5,5{\textquoteright},6,6{\textquoteright}-tetrahydroxy-3,3,3{\textquoteright},3{\textquoteright}-tetramethyl-1,1{\textquoteright}-spirobisindane (TTSBI) were carried out with 2,3,5,6-tetrafluoroterephthalonitrile (TFTPN) to obtain a homopolymer and copolymers, respectively. The organo-soluble polymers exhibited reasonably high molecular weights (23300-34,100 g/mol) and could be cast into self-standing films from their chloroform solutions. X-Ray diffraction studies indicated that PIMs were amorphous in nature. These polymers exhibited high thermal stability (T-10 = 490-510 degrees C) and possessed intrinsic microporosity with high BET surface area (360-796 m(2)/g). The gas permeation properties of SFX-PIM-25 and SFX-PIM-33 were evaluated and they exhibited high gas permeability (CO2 = 3595-4034 Barrer). The gas permeability data of SFX-PIM-25 and SFX-PIM-33 was located close to 1991 Robson upper bound for CO2/N-2, CO2/CH4 and O-2/N-2 gas pairs},
	issn = {1381-5148 },
	doi = {10.1016/j.reactfunctpolym.2018.10.008},
	author = {Shrimant, Bharat and Kharul, Ulhas K. and Wadgaonkar, Prakash P.}
}