@article { ISI:000229488700008,
	title = {Vapor phase oxidation of 4-fluorotoluene over vanadia-titania catalyst},
	journal = {Journal of Molecular Catalysis A - Chemical},
	volume = {234},
	number = {1-2},
	year = {2005},
	month = {JUN},
	pages = {51-57},
	publisher = {ELSEVIER SCIENCE BV},
	type = {Article},
	address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS},
	abstract = {<p>The vapor phase oxidation of 4-fluorotoluene has been carried out over vanadia-titania catalysts with moderate conversion and selectivity for 4-fluorobenzaldehyde. Two series of V2O5/TiO2 catalysts with 1-10 mol\% vanadia were prepared by sol-gel technique using vanadium and titanium peroxide as vanadia and titania precursors respectively and by impregnation technique using vanadium peroxide on anatase titania support. The samples were characterized by X-ray diffraction, NH3-TPD, FT-IR and BET surface area measurements. The XRD of the catalysts prepared by impregnation technique showed retention of the anatase titania whereas the catalysts prepared by sol-gel technique showed the formation of rutile titania with minor amount of anatase phase at lower vanadia content (1-3 \%), which completely transformed into anatase phase at higher vanadia loading. The samples prepared by sol-gel method showed higher acidity and surface area compared to the samples prepared by impregnation. Pyridine adsorption study by FT-IR revealed the presence of Lewis acidity at lower vanadia loading (1-3 \%) and presence of both Lewis as well as Bronsted acidity at higher vanadia loading. The catalytic activity for oxidation of 4-fluorotoluene increased with vanadia loading in the sol-gel catalysts. The catalysts prepared by impregnation technique were found to be less active. However the selectivity for 4-fluorobenzaldehyde decreased with increase in vanadia content. The influence of vanadia loading, reaction temperature and contact time on the catalytic activity for 4-fluorotoluene oxidation has been investigated. The structure of the catalyst and its catalytic activity has been correlated. (c) 2005 Elsevier B.V. All rights reserved.</p>},
	keywords = {Catalyst, fluorotoluene, Oxidation, vanadia-titania, vapor phase},
	issn = {1381-1169},
	doi = {10.1016/j.molcata.2005.02.020},
	author = {Maurya, S. K. and Patil, P. and Shubhangi B. Umbarkar and Gurjar, M. K. and Dongare, Mohan K. and Rudiger, S. and Kemnitz, E.}
}