	title = {Modifications in magnetic anisotropy of M-type strontium hexaferrite crystals by swift heavy ion irradiation},
	journal = {Journal of Magnetism and Magnetic Materials},
	volume = {305},
	number = {2},
	year = {2006},
	month = {OCT},
	pages = {392-402},
	publisher = {ELSEVIER SCIENCE BV},
	type = {Article},
	address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS},
	abstract = {<p>Using vibrating sample magnetometery (VSM) 50 MeV Li(3+) ion irradiation effects on magnetic properties of single crystals of SrGa(x)In(y)Fe(12-(x+y))O(19) (where x = 0, 5, 7, 9; y = 0, 0.8, 1.3, 1.0), are reported. The substitution of Ga and In in strontium hexaferrite crystals decreases the value of magnetization sharply, which is attributed to shifting of collinear magnetic order to a non-collinear one. Reduction of magnetization is also explained to be as a result of the occupation of the crystallographic sites of Fe(3+) by Ga(3+) and In(3+). The Li(3+) ion irradiation decreases the value of magnetization, irrespective of whether the crystals are Ga-In substituted or unsubstituted crystals of SrFe(12)O(19). The result is interpreted in terms of the occurrence of a paramagnetic doublet in crystals replacing magnetic sextuplet as a result of irradiation. Substitution of Ga-In in Strontium hexaferrite decreases the value of anisotropy constant. Irradiation with Li(3+) ions increases the values of anisotropy field for both substituted as well as unsubstituted crystals. Substitution with Ga-In also decreases the Curie temperature (T(c)) but the irradiation with Li(3+) ions does not affect the curie temperature of either Ga-In substituted or pure SrFe(12)O(19) crystals. (C) 2006 Elsevier B.V. All rights reserved.</p>},
	keywords = {anisotropy field, Curie temperature, irradiation, Magnetic anisotropy, Magnetization},