@article { ISI:000363466600014,
	title = {Synthesis and characterization of polyetherimides containing multiple ether linkages and pendent pentadecyl chains},
	journal = {Polymer International},
	volume = {64},
	number = {12},
	year = {2015},
	month = {DEC},
	pages = {1770-1778},
	publisher = {WILEY-BLACKWELL},
	address = {111 RIVER ST, HOBOKEN 07030-5774, NJ USA},
	abstract = {<p>4-(4-(4-(4-Aminophenoxy)-2-pentadecylphenoxy)phenoxy)aniline (APPPA) was synthesized starting from cashew nut shell liquid-derived bisphenol, i.e. 4-(4-hydroxyphenoxy)-3-pentadecylphenol, by nucleophilic substitution reaction with 4-chloronitrobenzene followed by reduction of the formed 4-(4-nitrophenoxy)-1-(4-(4-nitrophenoxy)phenoxy)-2-pentadecylbenzene. Three new polyetherimides containing multiple ether linkages and pendent pentadecyl chains were synthesized by one-step high-temperature solution polycondensation of APPPA in m-cresol with three aromatic dianhydrides, i.e. 3,3,4,4-oxydiphthalic anhydride, 4,4-(hexafluoroisopropylidene)diphthalic anhydride and 3,3,4,4-biphenyltetracarboxylic dianhydride. Inherent viscosities and number-average molecular weights of the polyetherimides were in the ranges 0.66-0.70 dLg(-1) and 17100-29700gmol(-1) (gel permeation chromatography, polystyrene standards), respectively, indicating the formation of reasonably high molecular weight polymers. The polyetherimides were soluble in organic solvents such as chloroform, dichloromethane, tetrahydrofuran, pyridine, m-cresol, N,N-dimethylformamide, N,N-dimethylacetamide, N-methylpyrrolidone and dimethylsulfoxide, and could be cast into transparent, flexible and tough films from their solutions in chloroform. The polyetherimides exhibited glass transition temperatures (T-g) in the range 113-131 degrees C. The lowering of T-g could be attributed to the combined influence of flexibilizing ether linkages and pentadecyl chains which act as packing-disruptive{\textquoteright} groups. The temperature at 10\% weight loss (T-10), determined from thermogravimetric analysis in nitrogen atmosphere, was in the range 460-470 degrees C demonstrating good thermal stability. The virtues of solubility and large gap between T-g and T-10 mean that the polyetherimides containing pendent pentadecyl chains have possibilities for both solution as well as melt processability. (c) 2015 Society of Chemical Industry</p>},
	keywords = {CNSL, ether linkage, pentadecyl, polyetherimide, processability},
	issn = {0959-8103},
	doi = {10.1002/pi.4978},
	author = {Tawade, Bhausaheb V. and Kulkarni, Arun D. and Wadgaonkar, Prakash P.}
}