%0 Journal Article %J Microporous and Mesoporous Materials %D 2011 %T Characterization of surface acid sites in tin-silicalite-1 (Sn-MFI) molecular sieve by X-ray photoelectron spectroscopy %A Niphadkar, P. S. %A Patil, K. R. %A Joshi, P. N. %K Lewis acidity %K Pyridine chemisorption %K SiO2/SnO2 molar ratio %K Sn-MFI %K XPS %X

The nature, strength and density of surface acid sites in Sn-MFI molecular sieves with different Sn-content were characterized by N 1s high resolution photoelectron peak of chemisorbed pyridine in combination with pyridine-IR and TPAD. Two peaks emerged at 399.5 +/- 0.2 and 401.5 +/- 0.2 eV by deconvoluting composite N is peak were assigned to chemisorbed pyridine on weak and relatively strong Lewis acid sites, respectively. The relative percentage of strong Lewis acid sites was found to increase with the decrease of framework Sn content. A close agreement was observed between the ratios of weak Lewis acid sites to strong Lewis acid sites obtained from XPS and TPAD. (C) 2010 Elsevier Inc. All rights reserved.

%B Microporous and Mesoporous Materials %I ELSEVIER SCIENCE BV %C PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS %V 141 %P 236-240 %8 MAY %G eng %N 1-3 %3 Foreign %4 3.58 %R 10.1016/j.micromeso.2010.10.036