02011nas a2200229   4500008004100000022001400041245009400055210006900149260010600218300001400324490000700338520114600345653001701491653002101508653002401529653001601553100002201569700002201591700001901613700002301632856012601655       2005                        eng d  a0014-305700aBenzoylation of polyphenylene oxide: characterization and gas permeability investigations0 aBenzoylation of polyphenylene oxide characterization and gas per  aTHE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, ENGLANDbPERGAMON-ELSEVIER SCIENCE LTDcOCT  a2461-24710 v413 a<p>Benzoylation of polyphenylene oxide (PPO) was carried out with aromatic acid chlorides bearing specific groups at para-position (H methyl, Br, Cl and nitro), which differ in their polarity and bulk. The reaction conditions were optimized individually to get the high degree of substitution. These materials were characterized for thermal as well as other physical properties that are known to affect the gas permeation. In a series investigated, the nitrobenzoyl substitution on PPO resulted in the highest increase in glass transition temperature and the lowest thermal stability. An estimation of the packing density parameters-fractional free volume by density measurement and the d-spacing by X-ray diffraction analysis showed an increase in the packing density. The gas permeability was found to decrease in all the cases of benzoylation. The helium and oxygen based selectivities were increased, while CO2 based selectivities were decreased. The unusual trend observed in the gas permeation properties is explained on the basis of nature of substituent and the degree of substitution. (c) 2005 Elsevier Ltd. All rights reserved.</p>10abenzoylation10aGas permeability10apolyphenylene oxide10aselectivity1 aBhole, Yogesh, S.1 aKharul, Ulhas, K.1 aSomani, S., P.1 aKumbharkar, S., C.  uhttp://library.ncl.res.in/content/benzoylation-polyphenylene-oxide-characterization-and-gas-permeability-investigations-002117nas a2200229   4500008004100000022001400041245010000055210006900155260010600224300001400330490000700344520125800351653001401609653001401623653001501637653002401652653001301676100002201689700002501711700002201736856012901758       2007                        eng d  a0014-305700aNitration and amination of polyphenylene oxide: synthesis, gas sorption and permeation analysis0 aNitration and amination of polyphenylene oxide synthesis gas sor  aTHE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, ENGLANDbPERGAMON-ELSEVIER SCIENCE LTDcAPR  a1450-14590 v433 a<p>A high degree of nitration of polyphenylene oxide (PPO) was successfully achieved by carefully optimizing synthetic protocol. The reduction of nitro group to amino could be done quantitatively. The physical properties of formed polymers were investigated and correlated with gas sorption and permeation properties. The formed polymers were amorphous in nature as revealed by wide angle X-ray diffraction spectra. An increase in the packing density in comparison to unsubstituted PPO as a result of induced polarity was indicated by lowering of fractional free volume and d-spacing. The substitution by either nitro or amino group increased the chain stiffness as revealed by the dynamic mechanical analysis. Though both, nitro and amino group substitution on PPO led to a decrease in pure gas permeability, the selectivity of various gas pairs was increased by these substitutions. The gas sorption analysis revealed that both, solubility selectivity and diffusivity selectivity were increased by these polar group substitutions. The nitro group substitution was more effective in improving solubility selectivity, while amino group substitution was more effective in improving diffusivity selectivity. (C) 2007 Elsevier Ltd. All rights reserved.</p>10aAmination10anitration10apermeation10apolyphenylene oxide10aSorption1 aBhole, Yogesh, S.1 aKaradkar, Prasad, B.1 aKharul, Ulhas, K.  uhttp://library.ncl.res.in/content/nitration-and-amination-polyphenylene-oxide-synthesis-gas-sorption-and-permeation-analysis