02464nas a2200253   4500008004100000022001400041245010100055210006900156260000900225300001400234490000700248520158800255653002701843653001601870653002001886653002601906100002201932700002501954700002101979700002502000700002602025700002802051856013102079       2019                        eng d  a0887-624X00aNew cardo bisphenol monomer containing pendant azido group and the resulting aromatic polyesters0 aNew cardo bisphenol monomer containing pendant azido group and t  cJUL   a1516-15260 v573 a<p>Expanding on our strategy to synthesize aromatic step-growth polymers containing pendant clickable azido groups via functional monomer approach, we have now designed and synthesized a new cardo bisphenol, viz., 2-(2-azidoethyl)-3, 3-bis(4-hydroxyphenyl) isoindolin-1-one (PPH-N-3). PPH-N-3 was conveniently synthesized starting from commercially available phenolphthalein by a three-step route in an overall yield of 65% using simple organic transformations. Aromatic (co)polyesters bearing pendant azido groups were synthesized by low-temperature solution polycondensation of PPH-N-3 or different molar ratios of PPH-N-3 and bisphenol-A (BPA) with aromatic diacid chlorides in dry dichloromethane in the presence of triethylamine (TEA) as a base. The formation of medium to reasonably high-molecular-weight (co)polyesters was evidenced from intrinsic viscosity and number-average molecular-weight measurements that were in the range 0.52-0.85 dL/g and 16,700-28,200, respectively. Tough, transparent, and flexible films could be cast from chloroform solutions of these (co)polyesters. (Co)polyesters were characterized using FTIR, H-1 NMR, C-13 NMR spectroscopy, XRD, and TGA. The thermal curing reaction of (co)polyesters involving decomposition of azido groups was studied by DSC analysis. The chemical modification of a representative copolyester containing pendant azido groups was carried out quantitatively using catalyst-free azide-maleimide cycloaddition reaction with two maleimides, namely, N-methylmaleimide and N-hexylmaleimide. (c) 2019 Wiley Periodicals, Inc.</p>
10aaromatic (co)polyester10aazido group10acardo bisphenol10aChemical modification1 aMaher, Deepak, M.1 aNagane, Samadhan, S.1 aJadhav, Uday, A.1 aSalunkhe, Pravin, H.1 aTawade, Bhausaheb, V.1 aWadgaonkar, Prakash, P.  uhttp://library.ncl.res.in/content/new-cardo-bisphenol-monomer-containing-pendant-azido-group-and-resulting-aromatic-polyesters02312nas a2200229   4500008004100000022001400041245006300055210005800118260000900176300001200185490000700197520155300204653003401757653003201791653002301823653003701846100002601883700002501909700002801934700002701962856009301989       2023                        eng d  a1060-132500aNorbornenyl-pendant aromatic (co)poly(ether ether ketone)s0 aNorbornenylpendant aromatic copolyether ether ketones  cNOV   a790-8000 v603 a<p>4, 4'-(Bicyclo (2.2.1) hept-5-en-2 yl methylene) bis (2-methoxyphenol) (BPA-NB) was utilized as a step-growth monomer for the synthesis of (co)poly(ether ether ketone)s (PEEK-NBs) via nucleophilic aromatic substitution polycondensation. A homo and five PEEK-NBs were synthesized by polycondensation of 4, 4'-difluorobenzophenone with BPA-NB and various compositions of BPA-NB and bisphenol-A, respectively. H-1 NMR spectroscopy confirmed the chemical structure and composition of PEEK-NBs. Inherent viscosity and number-average molecular weight values of PEEK-NBs were in the range 0.64 to 0.78 dL g(-1) and 62,670 to 84,470 g mol(-1), respectively, indicating the formation of polymers of reasonably high molecular weight. It was easy to dissolve PEEK-NBs in common organic solvents such as chloroform, dichloromethane, and tetrahydrofuran. Tough, transparent, and flexible films of PEEK-NBs could be cast from chloroform solution. X-Ray diffraction studies indicated amorphous nature of PEEK-NBs. Glass transition temperature (T-g) values, determined by DSC analysis, of PEEK-NBs were in the range 163 to190 degrees C and T-g values increased with the increase in mol % of BPA-NB. The post-polymerization modification of a representative PEEK-NB was demonstrated using two azido compounds, namely, 4-(azidomethyl)-7-methoxy-2H-chromen-2-one and 9-(azidomethyl)anthracene, via metal-free azide-alkene 1,3-dipolar cycloaddition reaction to obtain copoly(ether ether ketone)s appended with coumarinyl and anthracenyl moieties, respectively.</p>
10a(Co)poly(ether ether ketone)s10aazide-alkene click reaction10anorbornenyl groups10apost-polymerization modification1 aTalanikar, Aniket, A.1 aNagane, Samadhan, S.1 aWadgaonkar, Prakash, P.1 aRashinkar, Gajanan, S.  uhttp://library.ncl.res.in/content/norbornenyl-pendant-aromatic-copolyether-ether-ketones