01627nas a2200289 4500008004100000022001400041245008800055210006900143260007900212300001100291490000700302520063900309653002200948653001900970653001700989653002101006653002501027653001801052653002901070653001801099653001401117100001901131700002501150700001901175700002501194856011801219 2009 eng d a1098-012100aMagnetic characteristics of nanocrystalline multiferroic BiFeO3 at low temperatures0 aMagnetic characteristics of nanocrystalline multiferroic BiFeO3 aONE PHYSICS ELLIPSE, COLLEGE PK, MD 20740-3844 USAbAMER PHYSICAL SOCcAUG a0644230 v803 a
The magnetic characteristics of nanocrystalline BiFeO3 with average crystallite sizes of similar to 50 and similar to 100 nm are evaluated by studying the temperature and field dependence of magnetization at low temperatures. Different properties such as magnetization, coercivity, and remanence show evidence for changes in the magnetic properties associated with the phase transitions at low temperatures, reported from Raman studies. Detailed field-cooled and zero-field-cooled magnetization measurements show that the likely origin of the changes in the magnetic characteristics is from the changes in the domain structure.
10abismuth compounds10acoercive force10acrystallites10amagnetic domains10amagnetic transitions10aMultiferroics10aNanostructured materials10aRaman spectra10aremanence1 aVijayanand, S.1 aMahajan, Mangesh, B.1 aPotdar, H., S.1 aJoy, Pattayil, Alias uhttp://library.ncl.res.in/content/magnetic-characteristics-nanocrystalline-multiferroic-bifeo3-low-temperatures-0