01779nas a2200229 4500008004100000022001400041245011700055210006900172260007900241300001400320490000700334520086600341653002701207653003801234653003101272653003101303100002101334700002201355700002001377700002601397856012601423 2011 eng d a1044-580300aGrowth of hydrothermally stable meso-porous silica structure interconnected around micro-porous zeolite crystals0 aGrowth of hydrothermally stable mesoporous silica structure inte a360 PARK AVE SOUTH, NEW YORK, NY 10010-1710 USAbELSEVIER SCIENCE INCcDEC a1166-11720 v623 a
The growth of hydrothermally stable ordered meso-porous silica with M41S type structure interconnected around zeolite crystals was achieved from seeds normally nucleating the crystallization of micro-porous zeolite. The solid state NMR and FT-IR showed species like Si(OSi)(3)OH and Si(OSi)(2)(OH)(2) (or Q(3) and Q(2) sites, respectively) are formed during first hydrothermal treatment with surfactant and NaOH. These species and surface silanol group of zeolite crystal condense to give meso-porous silica structure interconnected around zeolite crystal during re-crystallization at lower pH. Resulting meso-micro-porous hybrid material is found to be highly active, selective and stable in the synthesis of 2-(phenylamino) ethanol from aniline and ethylene carbonate compare to parent ZSM-5 and pure MCM-41. (C) 2011 Elsevier Inc. All rights reserved.
10aHydrothermal stability10aInterconnected meso-porous silica10aMeso-micro hybrid material10aSynthesis of amino alcohol1 aKinage, Anil, K.1 aPrashar, Atul, K.1 aBerlier, Gloria1 aChaturvedi, Rajiv, K. uhttp://library.ncl.res.in/content/growth-hydrothermally-stable-meso-porous-silica-structure-interconnected-around-micro-0