@article { ISI:000279996500008, title = {Synthesis and characterization of new aromatic polyesters containing pendent naphthyl units}, journal = {Journal of Applied Polymer Science}, volume = {117}, number = {5}, year = {2010}, month = {SEP}, pages = {2545-2552}, publisher = {JOHN WILEY \& SONS INC}, address = {111 RIVER ST, HOBOKEN, NJ 07030 USA}, abstract = {

Two bisphenols, viz., 4,4{\textquoteright}-[1-(2-naphthaleny-1)ethylidene]bisphenol and 4,4{\textquoteright}-[1-(2-naphthalenyl) ethylidene]bis-3-methylphenol were prepared by condensation of commercially available 2-acetonaphthanone with phenol and o-cresol, respectively. A series of new aromatic polyesters containing pendent naphthyl units was synthesized by phase-transfer-catalyzed interfacial polycondensation of these bisphenols with isophthaloyl chloride, terephthaloyl chloride, and a mixture of isophthaloyl chlorideiterephthaloyl chloride (50 : 50 mol \%). Inherent viscosities of polyesters were in the range 0.83-1.76 dL g(-1), while number average molecular weights (M(n)) were in the range 61,000-235,000 g mol(-1). Polyesters were readily soluble in organic solvents such as dichloromethane, chloroform, tetrahydrofuran, m-cresol, pyridine, N,N-dimethylformamide, N,N-dimethylacetarnide, and 1-methyl-2-pyrrolidinone at room temperature. Tough, transparent, and flexible films were cast from a solution of polyesters in chloroform. X-Ray diffraction measurements displayed a broad halo at 20 congruent to 19 degrees indicating the amorphous nature of polyesters. Glass transition temperatures of polyesters were in the range 209-259 degrees C. The temperature at 10\% weight loss (T(10)), determined by TGA in nitrogen atmosphere, of polyesters was in the range 435-500 degrees C indicating their good thermal stability. (C) 2010 Wiley Periodicals, Inc. J Appl Polym Sci 117: 2545-2552, 2010

}, keywords = {Aromatic polyesters, bisphenol, interfacial polycondensation, pendent naphthyl units}, issn = {0021-8995}, doi = {10.1002/app.32162}, author = {Honkhambe, Pandurang N. and Biyani, Mahesh V. and Bhairamadgi, Nagendra S. and Wadgaonkar, Prakash P. and Salunkhe, Manikrao M.} } @article { ISI:000276790500011, title = {Synthesis and characterization of new aromatic polyesters containing cardo decahydronaphthalene groups}, journal = {European Polymer Journal}, volume = {46}, number = {4}, year = {2010}, month = {APR}, pages = {709-718}, publisher = {PERGAMON-ELSEVIER SCIENCE LTD}, address = {THE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, ENGLAND}, abstract = {

Three cardo bisphenols containing decahydronaphthalene group viz., 4,4{\textquoteright}-(octahydro-2(1H)-naphthylidene)bisphenol, 4,4{\textquoteright}-(octahydro-2(1H)-naphthylidene)bis-3-methylphenol and 4,4{\textquoteright}-(octahydro-2(1H)-naphthylidene)bis-3,5-dimethylphenol were synthesized starting from commercially available 2-naphthol and were utilized for synthesis of new aromatic polyesters by phase transfer-catalyzed interfacial polycondensation with isophthaloyl chloride, terephthaloyl chloride and a mixture of isophthaloyl chloride and terephthaloyl chloride (50:50 mol \%). Inherent viscosities and number average molecular weights (M(n)) of polyesters were in the range 0.35-0.84 dL/g and 13300-48,500 (Gel Permeation Chromatography, polystyrene standard), respectively. Polyesters were readily soluble in organic solvents such as dichloromethane, chloroform, tetrahydrofuran, meta-cresol, pyridine, N,N-dimethylformamide, N,N-dimethylacetamide, and 1-methy1-2-pyrrolidinone at room temperature and could be cast into tough, transparent and flexible films from their chloroform solutions. Wide-angle X-ray diffraction measurements revealed the amorphous nature of polyesters. The glass transition temperature of polyesters was in the range 207-287 degrees C. The temperature at 10\% weight loss (T(10)), determined from thermogravimetric analysis of polyesters, was in the range 425-460 degrees C indicating their good thermal stability. (C) 2010 Elsevier Ltd. All rights reserved.

}, keywords = {bisphenol, Cardo, Decahydronaphthalene, polyester, Structure-property relationship}, issn = {0014-3057}, doi = {10.1016/j.eurpolymj.2009.12.028}, author = {Honkhambe, Pandurang N. and Bhairamadgi, Nagendra S. and Biyani, Mahesh V. and Wadgaonkar, Prakash P. and Salunkhe, Manikrao M.} } @article { ISI:000293849200017, title = {Poly(ether ether ketone)s and poly(ether ether ketone ketone)s containing cardo decahydronaphthalene groups: synthesis and characterization}, journal = {Journal of Applied Polymer Science}, volume = {122}, number = {3}, year = {2011}, month = {NOV}, pages = {1607-1613}, publisher = {WILEY-BLACKWELL}, address = {COMMERCE PLACE, 350 MAIN ST, MALDEN 02148, MA USA}, abstract = {

New poly(ether ether ketone)s and poly (ether ether ketone ketone) s were synthesized by polycondensation of each of the three bisphenols, viz., 4,4{\textquoteright}-(octahydro-2(1H)-naphthylidene) bisphenol, 4,4{\textquoteright}-(octa-hydro-2(1H)-naphthylidene) bis-3-methylphenol, and 4,4{\textquoteright}(octahydro-2(1H)-naphthylidene) bis-3,5-dimethylphenol with 4,4{\textquoteright}-difluorobenzophenone and 1,3-bis(4-fluorobenzoyl) benzene in a mixture of N,N-dimethylacetamide and toluene [1 : 1 (v/v)] in the presence of anhydrous potassium carbonate. Inherent viscosities of poly(ether ether ketone) s and poly (ether ether ketone ketone) s were in the range 0.32-0.80 dL/g and number-average molecular weights were in the range 16,100-55,900 g/mol. Poly(ether ether ketone) s and poly(ether ether ketone ketone) s were soluble in organic solvents such as dichloromethane, chloroform, tetrahydrofuran, meta-cresol, pyridine, and 1-methyl-2-pyrrolidinone at room temperature and could be cast into tough, transparent, and flexible films from their chloroform solutions. Wide angle x-ray diffraction measurements revealed the amorphous nature of poly(ether ether ketone) s and poly (ether ether ketone ketone) s. The glass transition temperature poly(ether ether ketone) s and poly(ether ether ketone ketone) s were in the range 185-251 degrees C. The temperature at 10\% weight loss, determined from thermogravimetric analysis, of poly(ether ether ketone) s and poly(ether ether ketone ketone) s in nitrogen atmosphere was in the range 462-493 degrees C indicating their good thermal stability. (C) 2011 Wiley Periodicals, Inc. J Appl Polym Sci 122: 1607-1613, 2011

}, keywords = {bisphenol, cardo decahydronaphthalene, poly(ether ether ketone ketone)s, poly(ether ether ketone)s, Polycondensation, Thermal properties}, issn = {0021-8995}, doi = {10.1002/app.33921}, author = {Honkhambe, Pandurang N. and Pasale, Sharad K. and Bhairamadgi, Nagendra S. and Kumbhar, Kishor P. and Salunkhe, Manikrao M. and Wadgaonkar, Prakash P.} } @article { ISI:000319610100003, title = {Synthesis and characterization of poly(ether ether ketone)s and poly(ether ether ketone ketone) s containing pendant biphenyl and naphthyl groups}, journal = {High Performance Polymers}, volume = {25}, number = {3}, year = {2013}, month = {MAY}, pages = {260-267}, publisher = {SAGE PUBLICATIONS LTD}, address = {1 OLIVERS YARD, 55 CITY ROAD, LONDON EC1Y 1SP, ENGLAND}, abstract = {

New poly(ether ether ketone)s (PEEKs) and poly(ether ether ketone ketone)s (PEEKKs) containing pendant biphenyl and naphthyl groups were synthesized by nucleophilic substitution reaction of each of the four bisphenols viz., 1-(4- biphenylyl)- 1,1- bis(4- hydroxyphenyl) ethane, 1-(4- biphenylyl)- 1,1- bis(3- methyl, 4- hydroxyphenyl) ethane, 4,4{\textquoteright}-[1-(2- naphthalenyl) ethylidene] bis-phenol and 4,4{\textquoteright}-[1-(2- naphthalenyl) ethylidene] bis-3-methylphenol with 4,4{\textquoteright}- difluorobenzophenone and 1,3- bis(4- fluorobenzoyl) benzene in a solvent mixture of N,N-dimethylacetamide and toluene in the presence of anhydrous potassium carbonate. Inherent viscosities and number-average molecular weights of polymers were in the range of 0.42-0.86 dl/g and 2.40-7.55 x 10(4), respectively. PEEKs and PEEKKs were amorphous in nature and were readily soluble in a wide range of organic solvents and could be cast into flexible and tough films from chloroform solution. Glass transition temperature of PEEKs and PEEKKs were in the range of 180 degrees C -200 degrees C. T-10 values of PEEKs and PEEKKs were in the range of 424 degrees C-512 degrees C in nitrogen atmosphere, indicating their good thermal stability.

}, keywords = {biphenyl, bisphenol, naphthyl, poly(ether ether ketone ketone)s, poly(ether ether ketone)s, Polycondensation, Thermal properties}, issn = {0954-0083}, doi = {10.1177/0954008312462731}, author = {Honkhambe, Pandurang N. and Dhamdhere, Neelam A. and Tawade, Bhausaheb V. and Salunkhe, Manikrao M. and Wadgaonkar, Prakash P.} } @article {48402, title = {Post-polymerization modifiable aromatic (co)poly(ether sulfone)s possessing pendant norbornenyl groups based upon a new bisphenol}, journal = {European Polymer Journal}, volume = {176}, year = {2022}, month = {AUG }, pages = {111431}, type = {Article}, abstract = {

A new bisphenol possessing pendant norbornenyl group viz., 4, 4 {\textquoteleft}-(bicyclo (2.2.1) hept-5-en-2 yl methylene) bis (2-methoxyphenol) (BPA-NB) was synthesized by a single-step base-catalyzed condensation reaction of 5-norbor-nene-2-carboxaldehyde with guaiacol. NMR spectral data indicated formation of BPA-NB comprising of isomeric components. A series of (co)poly(ether sulfone)s possessing pendant norbornenyl groups was synthesized by nucleophilic aromatic substitution polycondensation of varying molar ratio of BPA-NB and bisphenol-A (BPA) with bis(4-fluorophenyl) sulfone. Inherent viscosity values and number average molecular weights of (co)poly (ether sulfone)s were in the range 0.67-1.01 dL/g and 75,400-1,16,300 g/mol, respectively indicating the formation of reasonably high molecular weight polymers. Tough, transparent, and flexible films could be cast from chloroform solutions of these (co)poly(ether sulfone)s. (Co)poly(ether sulfone)s were characterized using FT-IR, H-1 NMR and C-13 NMR spectroscopy, XRD, TGA and DSC analysis. The formation of random copoly(ether sulfone)s was demonstrated by( 13)C NMR analysis. The incorporation of BPA-NB into (co)poly(ether sulfone)s resulted into improvement in Tg values. BPA-NB-based (co)poly(ether sulfone)s offered possibilities for post -modifications involving either methoxyl or norbornenyl groups. A representative copoly(ether sulfone) (PSU-NB-2) possessing pendant norbornenyl groups was chemically modified via thiol-ene reaction with three representative thiol compounds, namely, 1-dodecanethiol, 2-furanmethanethiol and 2-mercaptoethanol to yield corresponding post-modified polymers in a quantitative manner. Additionally, it was demonstrated that copoly (ether sulfone) possessing pendant norbornenyl groups could be used to form insoluble cross-linked gel in the presence of a multifunctional thiol cross-linker.

}, keywords = {(Co)poly(ether sulfone)s, bisphenol, Cross -linking, Pendant norbornenyl groups, Thiol-ene reaction}, issn = {0014-3057}, doi = {10.1016/j.eurpolymj.2022.111431}, author = {Talanikar, Aniket A. and Nagane, Samadhan S. and Wadgaonkar, Prakash P. and Rashinkar, Gajanan S.} } @article {49317, title = {Catechol- and phenolic hydroxyl-functionalized partially bio-based (Co) poly(ether sulfone)s with multifarious applicability}, journal = {European Polymer Journal}, volume = {220}, year = {2024}, month = {NOV}, pages = {113484}, type = {Article}, abstract = {

A largely bio-based new bisphenol, namely, 4,4 {\textquoteleft}-((3,4-dimethoxyphenyl)methylene)-bis(2-methoxyphenol) (DMBM) was synthesized by the reaction of veratraldehyde with guaiacol. DMBM and varying compositions of DMBM and bisphenol A were polycondensed with bis(4-fluorophenyl) sulfone to afford reasonably high molecular weight film-forming (co)poly(ether sulfone)s possessing built-in methoxyl groups. T10 and Tg values of (co)poly(ether sulfone)s were in the range 382-478 degrees C and 171-187 degrees C, respectively indicating their good thermal stability and the values decreased with increase in mol \% incorporation of DMBM. The methoxyl groups present in (co)poly (ether sulfone)s were quantitatively de-blocked resulting in the formation of corresponding polymers possessing pendant catechol moieties and free phenolic hydroxyl groups. By virtue of the presence of these functional moieties, (co)poly(ether sulfone)s are amenable for post-polymerization modifications, and exhibited properties such as antimicrobial (23 mm against Staphylococcus aureus and 18 mm against Escherichia coli)), antioxidant (72 \% scavenger of free radicals), adhesive (2.24 MPa lap shear strength) and usefulness as redox-active agent in zinc-ion batteries. These data underscore the promise of DMBM as a versatile monomer of wider utility for the synthesis of functional (co)poly(ether sulfone)s capable of expanding their applicability beyond the conventional ones.

}, keywords = {(Co)poly(ether sulfone)s, adhesive, Antimicrobial, Antioxidant, bio-based, bisphenol, Zinc-ion batteries}, issn = {0014-3057}, doi = {10.1016/j.eurpolymj.2024.113484}, author = {Wale, Apparav K. and Jagtap, Ashish S. and Pandey, Priyanshi R. and Dastager, Syed G. and Shelke, Manjusha V. and Ambade, Ashootosh V. and Wadgaonkar, Prakash P.} }