@article {47029,
	title = {Enhanced electrocatalytic activity of PtRu/nitrogen and sulphur co-doped crumbled graphene in acid and alkaline media},
	journal = {Journal of Colloid and Interface Science},
	volume = {590},
	year = {2021},
	month = {MAY },
	pages = {154-163},
	type = {Article},
	abstract = {<p>The low mass activity and high price of pure platinum (Pt)-based catalysts predominantly limit their large-scale utilization in electrocatalysis. Therefore, the reduction of Pt amount while preserving the electrocatalytic efficiency represents a viable alternative. In this work, we prepared new PtRu2 nanoparticles supported on sulphur and nitrogen co-doped crumbled graphene with trace amounts of iron (PtRu2/PF) electrocatalysts. The PtRu2/PF catalysts exhibited enhanced electrocatalytic performance and stability for the hydrogen evolution reaction (HER) at pH = 0. Moreover, the prepared PtRu2/PF electrocatalyst displayed higher HER activity than commercial 20\% Pt/C. The PtRu2/PF catalyst achieved a current density of 10 mA cm(-2) at an overpotential value of only 22 mV for HER, performing better activity than many other Pt-based electrocatalysts. Besides, the PtRu2/PF revealed a good performance for the oxygen reduction reaction (ORR) and oxygen evolution reaction (OER) in alkaline media. The PtRu2/PF catalyst recorded a current density of 10 mA cm(-2) at an overpotential of only 270 mV for OER in KOH (1.0 M) solution and an onset potential of 0.96 V vs. RHE (at 1 mA cm(-2)) for ORR in KOH (0.1 M) solution. (C) 2021 Elsevier Inc. All rights reserved.</p>
},
	keywords = {HER, OER, ORR, PtRu2, Sulphur and nitrogen co-doped crumbled graphene},
	issn = {0021-9797},
	doi = {10.1016/j.jcis.2021.01.049},
	author = {Pang, Liuqing and Miao, Yuanyuan and Bhange, Siddheshwar N. and Barras, Alexandre and Addad, Ahmed and Roussel, Pascal and Amin, Mohammed A. and Kurungot, Sreekumar and Szunerits, Sabine and Boukherroub, Rabah}
}
@article {48210,
	title = {Improvement in oxygen evolution performance of NiFe layered double hydroxide grown in the presence of 1T-Rich MoS2},
	journal = {ACS Applied Materials \& Interfaces},
	volume = {14},
	year = {2022},
	month = {JUL},
	pages = {31951-31961},
	type = {Article},
	abstract = {<p>
	NiFe layered double hydroxide (NiFe LDH) grown in the presence of MoS2 (rich in 1T phase) shows exceptional performance metrics for alkaline oxygen evolution reaction (OER) in this class of composites. The as-prepared NiFe LDH/MoS2 composite (abbreviated as MNF) exhibits a low overpotential (eta(10)) of 190 mV; a low Tafel slope of 31 mV dec(-1); and more importantly, a high stability in its performance manifested by the delivery of current output for 45 h. It is important to note that this could be achieved with an exceedingly low loading of 0.14 mg cm(-2). The mass activity of this composite (97 A g(-1)) is about 14 times greater than that of the conventional RuO2 (7 A g(-1) ) at eta = 200 mV. When normalized with respect to the total metal content, a mass activity of 1000 A g(-1) (eta = 300 mV) was achieved. Impedance analysis further reveals that the significant reduction in charge-transfer resistance and hence high current density (5 times greater as compared to NiFe LDH at eta = 300 mV) observed for MNF is associated with interfacial adsorption kinetics of intermediates (R-1). Significant enhancement in the intrinsic activity of MNF over LDH has been observed through normalization of current with the electrochemically active surface area. Computational studies suggest that the Ni centers in the composite act as the active sites for OER, which is well-corroborated with the observed postreaction appearance of Ni3+ species.</p>
},
	keywords = {Impedance, LDH-MoS2 hybrid electrocatalyst, mass activity, OER, overpotential},
	issn = {1944-8244},
	doi = {10.1021/acsami.2c06210},
	author = {Chakraborty, Soumita and Marappa, Shivanna and Agarwal, Sakshi and Bagchi, Debabrata and Rao, Ankit and Vinod, Chathakudath P. and Peter, Sebastian C. and Singh, Abhishek and Eswaramoorthy, Muthusamy}
}