@article { ISI:000228253200008, title = {Preparation of nanocrystalline ferroelectric BaNb(2)O6 by citrate gel method}, journal = {Bulletin of Materials Science}, volume = {28}, number = {2}, year = {2005}, month = {APR}, pages = {121-123}, publisher = {INDIAN ACADEMY SCIENCES}, address = {C V RAMAN AVENUE, SADASHIVANAGAR, P B \#8005, BANGALORE 560 080, INDIA}, abstract = {

A gel was formed when a aqueous solution of BaCl2, NbF5 and citric acid in stoichiometric ratio is heated on a water bath. This gel on decomposition at 600 degrees C yielded the nano crystallites of BaNb2O6, as confirmed by X-ray diffraction study (XRD). This is a much lower temperature as compared to that prepared by traditional solid state method (1000 degrees C) as reported for the formation of BaNb2O6. Transmission electron microscopic. (TEM) investigations revealed that the average particle size is 50 nm for the calcined powders. The room temperature dielectric constant at 1 kHz is found to be 1000. The ferroelectric hysteresis loop parameters of these samples were also studied.

}, keywords = {Ceramics, Chemical synthesis, electronic material, ferroelectricity, Oxides}, issn = {0250-4707}, doi = {10.1007/BF02704230}, author = {Gaikwad, S. P. and Samuel, V and Pasricha, R and Ravi, V} } @article { ISI:000230877900002, title = {Preparation of nanocrystalline ferroelectric CaBi2Ta2O9 by the urea method}, journal = {Ceramics International}, volume = {31}, number = {6}, year = {2005}, month = {JAN }, pages = {773-775}, publisher = {ELSEVIER SCI LTD}, type = {Article}, address = {THE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, OXON, ENGLAND}, abstract = {

A precipitate was formed when a aqueous solution of CaCl2, BiCl3, TaF5 and urea in stoichiometric ratio (total metal cations to urea ratio is 5) is heated on a water bath. This precipitate on decomposition at 600 degrees C yielded the nanocrystallites of ternary oxide CaBi2Ta2O9 (CBT) as confirmed by X-ray diffraction (XRD). Particle size and morphology was studied by transmission electron spectroscopy (TEM). Ferroelectric hysteresis loop parameters such as remnant polarization (P-r) and coercive field (E-C) were also determined. TEM investigations revealed that the average particle size of the polycrystalline powder is 70 nm. The room temperature dielectric constant was found to be 110. (c) 2004 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

}, keywords = {dielectric properties, Electron microscopy, ferroelectric properties, powders : chemical preparation}, issn = {0272-8842}, doi = {10.1016/j.ceramint.2004.08.011}, author = {Gaikwad, S. P. and Pasricha, R and Ravi, V} } @article { ISI:000227447800010, title = {Preparation of nanocrystalline ferroelectric CaBi2TaO9 by citrate gel method}, journal = {Materials Science and Engineering B-Solid State Materials for Advanced Technology}, volume = {117}, number = {2}, year = {2005}, month = {MAR}, pages = {159-161}, publisher = {ELSEVIER SCIENCE SA}, type = {Article}, address = {PO BOX 564, 1001 LAUSANNE, SWITZERLAND}, abstract = {

A gel was formed when an aqueous solution of CaCl2, BiCl3, TaF5 and citric acid in stoichiometric ratio is heated on a water bath. This gel on decomposition at 600degreesC yielded the nano-crystallites of ternary oxide, CaBi2Ta2O9 (CBT) as confirmed by X-ray diffraction study (XRD). Particle size and morphology was studied by transmission electron spectroscopy (TEM). Ferroelectric hysteresis loop parameters such as remnant polarization (P-r) and coercive field (E-C) are also determined. TEM investigations revealed that the average particle size of the polycrystalline powder is 40 nm. The room temperature dielectric constant was found to be 90. (C) 2004 Elsevier B.V All rights reserved.

}, keywords = {Bismuth, diffraction, Electron microscopy}, issn = {0921-5107}, doi = {10.1016/j.mseb.2004.11.006}, author = {Gaikwad, S. P. and Pasricha, R and Ravi, V} }