@article { ISI:000308310100032,
	title = {Control of porosity by using isoreticular zeolitic imidazolate frameworks (IRZIFs) as a template for porous carbon synthesis},
	journal = {Chemistry-A European Journal},
	volume = {18},
	number = {36},
	year = {2012},
	month = {SEP},
	pages = {11399-11408},
	publisher = {WILEY-V C H VERLAG GMBH},
	address = {BOSCHSTRASSE 12, D-69469 WEINHEIM, GERMANY},
	abstract = {<p>Herein, by using isoreticular zeolitic imidazolate frameworks (IRZIFs) as a template, we report the synthesis, morphology, and gas adsorption properties of porous carbon synthesized by a nanocasting method at 1000 degrees C, in which furfuryl alcohol (FA) was used as a carbon source. By using IRZIFs with variable porosity as templates, we could achieve control over the carbon porosity and H-2 and CO2 uptake. The resultant microporous carbon C-70, synthesized by using ZIF-70 as the template, is the most porous (Brunauer-Emmett-Teller (BET) surface area 1510 m(2)g(-1)). Carbon C-68, synthesized by using ZIF-68, has moderate porosity (BET surface area 1311 m(2)g(-1)), and C-69, synthesized by using ZIF-69, has the lowest porosity in this series (BET surface area 1171 m(2)g(-1)). The porous carbons C-70, C-68, and C-69, which have graphitic texture, have promising H2 uptake capacities of 2.37, 2.15, and 1.96 wt\%, respectively, at 77 K and 1 atm. Additionally, C-70, C-68, and C-69 show CO2 uptake capacities of 5.45, 4.98, and 4.54 mmolg(-1), respectively, at 273 K and 1 atm. The gas uptake trends shown by C-70, C-68, and C-69 clearly indicate the dependence of carbon porosity on the host template. Moreover, the as-synthesized carbons C-70, C-68, and C-69 show variable conductivity.</p>},
	keywords = {Carbon, Hydrogen storage, metal-organic frameworks, microporous materials, zinc},
	issn = {0947-6539},
	doi = {10.1002/chem.201200957},
	author = {Pachfule, Pradip and Biswal, Bishnu P. and Banerjee, Rahul}
}
@article { ISI:000325849000034,
	title = {Zeolitic imidazolate framework (ZIF)-derived, hollow-core, nitrogen-doped carbon nanostructures for oxygen-reduction reactions in PEFCs},
	journal = {Chemistry-A European Journal},
	volume = {19},
	number = {28},
	year = {2013},
	month = {JUL},
	pages = {9335-9342},
	publisher = {WILEY-V C H VERLAG GMBH},
	address = {BOSCHSTRASSE 12, D-69469 WEINHEIM, GERMANY},
	abstract = {<p>The facile synthesis of a porous carbon material that is doped with iron-coordinated nitrogen active sites (FeNC-70) is demonstrated by following an inexpensive synthetic pathway with a zeolitic imidazolate framework (ZIF-70) as a template. To emphasize the possibility of tuning the porosity and surface area of the resulting carbon materials based on the structure of the parent ZIF, two other ZIFs, that is, ZIF-68 and ZIF-69, are also synthesized. The resulting active carbon material that is derived from ZIF-70, that is, FeNC-70, exhibits the highest BET surface area of 262m2g-1 compared to the active carbon materials that are derived from ZIF-68 and ZIF-69. The HR-TEM images of FeNC-70 show that the carbon particles have a bimodal structure that is composed of a spherical macroscopic pore (about 200nm) and a mesoporous shell. X-ray photoelectron spectroscopy (XPS) reveals the presence of Fe-N-C moieties, which are the primary active sites for the oxygen-reduction reaction (ORR). Quantitative estimation by using EDAX analysis reveals a nitrogen content of 14.5wt.\%, along with trace amounts of iron (0.1wt.\%), in the active FeNC-70 catalyst. This active porous carbon material, which is enriched with Fe-N-C moieties, reduces the oxygen molecule with an onset potential at 0.80V versus NHE through a pathway that involves 3.3-3.8e- under acidic conditions, which is much closer to the favored 4e- pathway for the ORR. The onset potential of FeNC-70 is significantly higher than those of its counterparts (FeNC-68 and FeNC-69) and of other reported systems. The FeNC-based systems also exhibit much-higher tolerance towards MeOH oxidation and electrochemical stability during an accelerated durability test (ADT). Electrochemical analysis and structural characterizations predict that the active sites for the ORR are most likely to be the insitu generated NFeN2+2/C moieties, which are distributed along the carbon framework.</p>},
	keywords = {Doping, Electrochemistry, metal-organic frameworks, Nanostructures, oxygen-reduction reaction},
	issn = {0947-6539},
	doi = {10.1002/chem.201300145},
	author = {Palaniselvam, Thangavelu and Biswal, Bishnu P. and Banerjee, Rahul and Kurungot, Sreekumar}
}