@article { ISI:000228253200008, title = {Preparation of nanocrystalline ferroelectric BaNb(2)O6 by citrate gel method}, journal = {Bulletin of Materials Science}, volume = {28}, number = {2}, year = {2005}, month = {APR}, pages = {121-123}, publisher = {INDIAN ACADEMY SCIENCES}, address = {C V RAMAN AVENUE, SADASHIVANAGAR, P B \#8005, BANGALORE 560 080, INDIA}, abstract = {

A gel was formed when a aqueous solution of BaCl2, NbF5 and citric acid in stoichiometric ratio is heated on a water bath. This gel on decomposition at 600 degrees C yielded the nano crystallites of BaNb2O6, as confirmed by X-ray diffraction study (XRD). This is a much lower temperature as compared to that prepared by traditional solid state method (1000 degrees C) as reported for the formation of BaNb2O6. Transmission electron microscopic. (TEM) investigations revealed that the average particle size is 50 nm for the calcined powders. The room temperature dielectric constant at 1 kHz is found to be 1000. The ferroelectric hysteresis loop parameters of these samples were also studied.

}, keywords = {Ceramics, Chemical synthesis, electronic material, ferroelectricity, Oxides}, issn = {0250-4707}, doi = {10.1007/BF02704230}, author = {Gaikwad, S. P. and Samuel, V and Pasricha, R and Ravi, V} } @article { ISI:000230275100022, title = {Preparation of nanocrystalline LiNbO3 by citrate gel method}, journal = {Materials Letters}, volume = {59}, number = {19-20}, year = {2005}, month = {AUG}, pages = {2476-2478}, publisher = {ELSEVIER SCIENCE BV}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

A gel was formed when an aqueous solution of Li(NO3) NbF5 and citric acid in stoichiometric ratio is heated in a water bath at 100 degrees C. This gel on decomposition at 700 degrees C produced the fine crystallites of ternary oxide, LiNbO3 (LN). The phase contents and lattice parameters were studied by the powder X-ray diffraction (XRD). Particle size and morphology was studied by transmission electron spectroscopy (TEM). (c) 2005 Elsevier B.V. All rights reserved.

}, keywords = {Ceramics, Electron microscopy, electronic materials, lithium niobate, X-ray diffraction}, issn = {0167-577X}, doi = {10.1016/j.matlet.2005.03.028}, author = {Navale, SC and Samuel, V and Ravi, V} } @article { ISI:000231605600002, title = {Preparation of ultrafine LiTaO3 powders by citrate gel method}, journal = {Bulletin of Materials Science}, volume = {28}, number = {5}, year = {2005}, month = {AUG}, pages = {391-393}, publisher = {INDIAN ACADEMY SCIENCES}, type = {Article}, address = {C V RAMAN AVENUE, SADASHIVANAGAR, P B \#8005, BANGALORE 560 080, INDIA}, abstract = {

A gel was formed when a aqueous solution of Li(NO3), TaF5 and citric acid in stoichiometric ratio was heated in a water bath. This gel on decomposition at 700 degrees C produced fine crystallites of ternary oxide, LiTaO3 (LT). The phase contents and lattice parameters were studied by powder X-ray diffraction (XRD). Particle size and morphology were studied by transmission electron spectroscopy (TEM).

}, keywords = {Ceramics, Electron microscopy, electronic materials, X-ray diffraction}, issn = {0250-4707}, doi = {10.1007/BF02711224}, author = {Navale, SC and Samuel, V and Ravi, V} }