@article { ISI:000238294800037, title = {Suppression of electron-transfer characteristics of ferrocene by OTS monolayer on a silicon/electrolyte interface}, journal = {Journal of Colloid and Interface Science}, volume = {299}, number = {2}, year = {2006}, month = {JUL}, pages = {777-784}, publisher = {ACADEMIC PRESS INC ELSEVIER SCIENCE}, type = {Article}, address = {525 B ST, STE 1900, SAN DIEGO, CA 92101-4495 USA}, abstract = {

The passivating behavior of self-assembled monolayers (SAMs) of octadecyltrichlorosilane (OTS) on an n-type Si(100) electrode with and without a redox species like ferrocene in a polar non-aqueous medium has been investigated using techniques like contact angle measurements, Fourier transform infrared (FTIR) spectroscopy and X-ray photoelectron spectroscopy (XPS) to understand the role of the monolayer. The electron-transfer behavior of ferrocene is found to be drastically affected by the presence of monolayer and the reasons for these are analyzed as a function of the change in resistance, dielectric thickness and coverage of the monolayer. Electrochemical impedance analysis in the presence of ferrocene gives the monolayer coverage as 0.998 and the apparent rate constant calculated from this gives 4.85 x 10(-12) cm s(-1) in comparison with 4.4 x 10(-8) cm s(-1) for a similar electrode without any monolayer. A positive shift of 200 mV in the flat-band potential after monolayer formation also suggests the covalent coupling of the silane nionolayer offering a protective barrier. (c) 2006 Elsevier Inc. All rights reserved.

}, keywords = {cyclic voltammetry, ferrocene, impedance analysis, octadecyltrichlorosilane (OTS), rate constant, self-assembled monolayer (SAM)}, issn = {0021-9797}, doi = {10.1016/j.jcis.2006.03.013}, author = {Kulkarni, S. A. and Kakade, Bhalchandra A. and Mulla, Imtiaz S. and Pillai, V. K.} } @article { ISI:000243695000025, title = {Synthesis and characterization of mesoporous carbon through inexpensive mesoporous silica as template}, journal = {Microporous and Mesoporous Materials}, volume = {98}, number = {1-3}, year = {2007}, month = {JAN}, pages = {189-199}, publisher = {ELSEVIER SCIENCE BV}, type = {Article}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

Mesoporous silica materials have been synthesized through sol-gel reaction using inexpensive sodium silicate as source of silica and low cost hydroxy carboxylic acid compounds as templates/pore forming agents. The material measured surface area of 1014 m(2)/g, pore diameter of 65 angstrom and pore volume of 1.4 cc/g when parameters like time and temperature of synthesis along with mole ratio of TA/SiO(2) were optimized. Here TA stands for tartaric acid. Carbonization of sucrose inside the pores of above silica material at 900 degrees C followed by removal of silica framework using aqueous ethanoic solution of NaOH gave rise to mesoporous carbon material. The resulting materials were characterized by N(2)-sorption, FTIR spectroscopy, X-ray diffraction, transmission electron microscopy, X-ray photoelectron spectroscopy, thermal analysis and cyclic voltammetry. Three dimensional interconnecting wormhole channel arrangement of mesoporous silica template leads to mesoporous carbon replica with surface area of 1200 m(2)/g. X-ray photoelectron spectroscopic study (XPS) of the mesoporous carbon material shows the concentration of carbon atom in the range of 97-98\% with 1-2\% oxygen and negligible amount of silica. The electrochemical double layer capacitance behavior of carbon material with the specific capacitance value of 88.0 F/g at the scan rate of 1 mV/s appears to be promising. (C) 2006 Elsevier Inc. All rights reserved.

}, keywords = {Electrochemical properties, hydroxy carboxylic acid, mesoporous carbon, Mesoporous silica, sodium silicate}, issn = {1387-1811}, doi = {10.1016/j.micromeso.2006.09.003}, author = {Karandikar, Prashant R. and Patil, K. R. and Mitra, A. and Kakade, Bhalchandra A. and Chandwadkar, Asha J.} } @article { ISI:000280514500009, title = {Synthesis of Rh-carbon nanotube based heterostructures and their enhanced field emission characteristics}, journal = {Chemical Communications}, volume = {46}, number = {31}, year = {2010}, month = {JUL}, pages = {5671-5673}, publisher = {ROYAL SOC CHEMISTRY}, address = {THOMAS GRAHAM HOUSE, SCIENCE PARK, MILTON RD, CAMBRIDGE CB4 0WF, CAMBS, ENGLAND}, abstract = {

Selective decoration of Rh nanospheres on acid functionalized carbon nanotubes has been demonstrated using Al as a sacrificial substrate. Remarkable field emission has been observed for this heterostructure as a high current density of 170 mu A cm(-2) is generated at an ultra-low threshold of 300 V mu m(-1), compared to much smaller values for Rh nanospheres and carbon nanotubes separately.

}, issn = {1359-7345}, doi = {10.1039/c0cc01532f}, author = {Sathe, Bhaskar R. and Kakade, Bhalchandra A. and Kushwaha, Ajay and Aslam, Mohammed and Pillai, Vijayamohanan K.} }