@article {45881, title = {Nitrogen-induced surface area and conductivity modulation of carbon nanohorn and its function as an efficient metal-free oxygen reduction electrocatalyst for anion-exchange membrane fuel cells}, journal = {SMALL}, volume = {11}, year = {2015}, month = {JAN }, pages = {352-360}, type = {Article}, abstract = {

Nitrogen-doped carbon morphologies have been proven to be better alternatives to Pt in polymer-electrolyte membrane (PEM) fuel cells. However, efficient modulation of the active sites by the simultaneous escalation of the porosity and nitrogen doping, without affecting the intrinsic electrical conductivity, still remains to be solved. Here, a simple strategy is reported to solve this issue by treating single-walled carbon nanohorn (SWCNH) with urea at 800 degrees C. The resulting nitrogen-doped carbon nanohorn shows a high surface area of 1836 m(2) g(-1) along with an increased electron conductivity, which are the pre-requisites of an electro catalyst. The nitrogen-doped nanohorn annealed at 800 degrees C (N-800) also shows a high oxygen reduction activity (ORR). Because of the high weight percentage of pyridinic nitrogen coordination in N-800, the present catalyst shows a clear 4-electron reduction pathway at only 50 mV overpotential and 16 mV negative shift in the half-wave potential for ORR compared to Pt/C along with a high fuel selectivity and electrochemical stability. More importantly, a membrane electrode assembly (MEA) based on N-800 provides a maximum power density of 30 mW cm(-2) under anion-exchange membrane fuel cell (AEMFC) testing conditions. Thus, with its remarkable set of physical and electrochemical properties, this material has the potential to perform as an efficient Pt-free electrode for AEMFCs.

}, issn = {1613-6810}, doi = {10.1002/smll.201303892}, author = {Unni, SreeKuttan M. and Bhange, Siddheshwar N. and Illathvalappil, Rajith and Mutneja, Nisha and Patil, Kasinath R. and Kurungot, Sreekumar} } @article { ISI:000374790700031, title = {Nitrogen and sulphur co-doped crumbled graphene for the oxygen reduction reaction with improved activity and stability in acidic medium}, journal = {Journal of Materials Chemistry A}, volume = {4}, number = {16}, year = {2016}, month = {MAR}, pages = {6014-6020}, publisher = {ROYAL SOC CHEMISTRY}, type = {Article}, address = {THOMAS GRAHAM HOUSE, SCIENCE PARK, MILTON RD, CAMBRIDGE CB4 0WF, CAMBS, ENGLAND}, abstract = {

Non-precious dioxygen reduction electrocatalysts have attracted great attention nowadays for the development of stable, cost-effective proton exchange membrane fuel cells. In line with the development of non-precious electrocatalysts, here we report the synthesis of a platinum-free oxygen reduction electrocatalyst based on nitrogen and sulphur co-doped crumbled graphene with trace amounts of iron. The co-doped crumbled graphene structure was obtained by simple oxidative polymerisation of ethylenedioxythiophene in aqueous solution followed by an annealing process under an inert atmosphere. This new electrocatalyst displays improved oxygen reduction activity and electrochemical stability under acidic conditions. The half-cell reaction of the 1000 degrees C annealed polyethylenedioxythiophene (PF-1000) displays only 0.1 V overpotential in both the onset and half-wave potentials compared to state-of-the-art Pt/C in an acidic environment for the ORR. More importantly, the limiting current of PF-1000 clearly surpasses the limiting current displayed by Pt/C, indicating that the crumbled assembly of the graphene flakes helps the system to expose the active sites and the porous network of the material matrix ensures extended accessibility of active sites to the electrolyte and reagent. The dioxygen reduction kinetics of PF-1000 appear similar to those of Pt/C and the system accomplishes the reduction of the dioxygen molecule through the recommended four-electron reduction pathway. The improved activity and electrochemical stability of PF-1000 are mainly attributed to the enriched and well accessible active reaction centres such as graphitic nitrogen, sulphur, and iron coordination and the peculiar morphology of PF-1000. Further, a single cell evaluation of a membrane electrode assembly based on PF-1000 as the cathode catalyst delivered a maximum power density of 193 mW cm(-2) at a cell temperature of 60 degrees C using Nafion as the proton conducting membrane.

}, issn = {2050-7488}, doi = {10.1039/c6ta00073h}, author = {Bhange, Siddheshwar N. and Unni, SreeKuttan M. and Kurungot, Sreekumar} } @article {43844, title = {Nitrogen-doped graphene anchored with mixed growth patterns of CuPt alloy nanoparticles as a highly efficient and durable electrocatalyst for the oxygen reduction reaction in an alkaline medium}, journal = {Nanoscale}, volume = {9}, year = {2017}, month = {JUL}, pages = {9009-9017}, type = {Article}, abstract = {

A highly active and durable CuPt alloy catalyst with trigonal bipyramidal and truncated cube-type mixed morphologies, anchored on the nitrogen-doped graphene (NGr) surface (CuPt-TBTC/NGr), was prepared by a simple and fast method. The obtained CuPt alloy showed improved oxygen reduction reaction (ORR) activity, with a 30 mV positive shift in the half-wave potential value, as compared to the state-of-the-art Pt/C catalyst in a 0.1 M KOH solution. The CuPt alloy with the trigonal bipyramidal morphology possesses porous type inter-connected sides, which help to achieve improved mass transport of oxygen during the ORR. The exposure of the (111) plane of the CuPt alloy further improved the catalytic activity towards the dioxygen reduction in alkaline media. The ORR activity of the NGr-supported CuPt alloy was found to be dependent on the reaction time, and improved activity was obtained on the material derived at a reaction time of 90 min (CuPt-TBTC/NGr-90). The material synthesized at a lower or higher reaction time than 90 min resulted in a partially formed trigonal bipyramidal morphology with more truncated cubes or agglomerated trigonal bipyramidal and truncated cubes with closed type structures, respectively. Along with the high intrinsic ORR activity, CuPt-TBTC/NGr-90 displayed excellent electrochemical stability. Even after repeated 1000 potential cycling in a window ranging from 0.10 to 1.0 V (vs. RHE), the system clearly outperformed the state-of-the-art Pt/C catalyst with 15 and 60 mV positive shifts in the onset and half-wave potentials, respectively. CuPt-TBTC/NGr-90 also exhibited 2.1 times higher mass activity and 2.2 times higher specific activity, compared to Pt/C at 0.90 V (vs. RHE). Finally, a zinc-air battery fabricated with the alloy catalyst as the air electrode displayed a peak power density of 300 mW cm(-2), which is much higher than the peak power density of 253 mW cm(-2) obtained for the state-of-the-art Pt/C catalyst as the air electrode.

}, doi = {10.1039/c7nr00697g}, author = {Illathvalappil, Rajith and Dhavale, Vishal M. and Bhange, Siddheshwar N. and Kurungot, Sreekumar} }