@article { ISI:000228436200035, title = {Self-assembly of nanostructured PbS for solar photovoltaic applications}, journal = {Materials Chemistry and Physics}, volume = {91}, number = {2-3}, year = {2005}, month = {JUN}, pages = {447-453}, publisher = {ELSEVIER SCIENCE SA}, type = {Article}, address = {PO BOX 564, 1001 LAUSANNE, SWITZERLAND}, abstract = {

In the present communication, the self-assembly of nanocrystalline PbS at the liquid-liquid interface is reported. The PbS nanocrystals were, subsequently, transformed in the form of thin films by dip coating. The resultant Q-PbS films were characterized by SEM-EDAX, TEM-SAED, XRD, XPS and UV-vis Spectroscopy. Pyramidal features at the nanometer scale, preferred orientation along (2 2 0) and (4 0 0) planes of cubic structure and a sharp excitonic peak at 656 run are the salient aspects of this work. The band-gap of the order of 1.8 eV (associated with the excitonic feature) is ideally suited for solar photovoltaic applications. (c) 2004 Elsevier B.V. All rights reserved.

}, keywords = {Liquid-liquid interface, nanopyramid, Nanostructures, PbS}, issn = {0254-0584}, doi = {10.1016/j.matchemphys.2004.12.007}, author = {Hawaldar, Ranjit R. and Kanade, K. G. and Patil, K. R. and Sathaye, S. D. and Mulik, Uttam P. and Amalnerkar, Dinesh P.} } @article { ISI:000230375200016, title = {Synthesis of fine PbE (E = S, Se) powder from direct in situ reduction of sulphur or selenium}, journal = {Materials Chemistry and Physics}, volume = {93}, number = {1}, year = {2005}, month = {SEP}, pages = {91-94}, publisher = {ELSEVIER SCIENCE SA}, type = {Article}, address = {PO BOX 564, 1001 LAUSANNE, SWITZERLAND}, abstract = {

Lead sulphide and lead selenide have been prepared for the first time, by in situ reduction of elemental S or Se by using aqueous DMF or aqueous SFS as reducing agents and their reaction with lead acetate. The grayish-black powder has been characterized by powder XRD measurement, XPS and SEM/EDAX analysis. Powder X-ray diffraction pattern revealed that cubic PbE (E = S, Se) is formed with a little impurities of lead in case of PbSe. Slightly broader peaks in XRD measurement suggest small particles diameter in the powder. The particle size by using Scheffer{\textquoteright}s formula is found to be about 100 nm. Peaks due to free lead particles are observed in XPS and EDS (in case of PbSe) analysis and SEM analysis indicates agglomerated particles. (c) 2005 Elsevier B.V All rights reserved.

}, keywords = {Chemical synthesis, electronic materials, reduction, Semiconductor}, issn = {0254-0584}, doi = {10.1016/j.matchemphys.2005.02.025}, author = {Khanna, P. K. and Subbarao, VVVS and Wagh, M. and Jadhav, P. and Patil, K. R.} } @article { ISI:000238050700006, title = {Synthesis of beta-Ag2Se from organo-selenium precursor and silver nitrate in DMF via simultaneous reduction of selenium and silver salt}, journal = {Materials Letters}, volume = {60}, number = {17-18}, year = {2006}, month = {AUG}, pages = {2080-2085}, publisher = {ELSEVIER SCIENCE BV}, type = {Article}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

Reaction of selenium powder and silver nitrate in aqueous N,N{\textquoteright}-dimethylformamide (aq. DMF) leads to formation of silver selenide. Similar reaction with cycloalkeno-1,2,3-selenadiazole an organic compound of selenium upon thermolysis, also produces silver selenide. It is believed that DMF activates selenium and reduces silver salt via in-situ generated hydrogen ion simultaneously. Slightly broadened X-ray diffraction pattern for pure beta silver selenide (beta-Ag2Se) was observed. Scanning electron microscopy (SEM) indicated that the agglomerated particles could be in the range of about 100 to 200 nm in dimension. EDAX analysis showed non-stoichiometric elemental ratio between silver and selenium. It is found that the weight percent of Ag is slightly higher than Se. However, free amorphous selenium is also detected by XPS analysis when the product is made by use of elemental selenium. Thermal analysis (TGA) revealed a small (4\%) weight loss due to the presence of organics or the solvent from the reaction medium. (c) 2005 Elsevier B.V. All rights reserved.

}, keywords = {Chemical synthesis, nano powder, noble metal chalcogenides, Semiconductor}, issn = {0167-577X}, doi = {10.1016/j.matlet.2005.12.079}, author = {Khanna, P. K. and Singh, N. and Charan, Shobhit and Patil, K. R.} } @article { ISI:000244765100003, title = {Studies on gas sensing performance of pure and modified barium strontium titanate thick film resistors}, journal = {Bulletin of Materials Science}, volume = {30}, number = {1}, year = {2007}, month = {FEB}, pages = {9-17}, publisher = {INDIAN ACADEMY SCIENCES}, type = {Article}, address = {C V RAMAN AVENUE, SADASHIVANAGAR, P B \#8005, BANGALORE 560 080, INDIA}, abstract = {

Barium strontium titanate ((Ba0.87Sr0.13)TiO3-BST) ceramic powder was prepared by mechanochemical process. The thick films of different thicknesses of BST were prepared by screen-printing technique and gas-sensing performance of these films was tested for various gases. The films showed highest response and selectivity to ammonia gas. The effect of film thickness on gas response was also studied. As prepared BST thick films were surface modified by dipping them into an aqueous solution of titanium chloride (TiCl3) for different intervals of time. Surface modification shifted response to H2S gas suppressing the responses to ammonia and other gases. The surface modification, using dipping process, altered the adsorbate-adsorbent interactions, which gave the unusual sensitivity and selectivity effect. Sensitivity, selectivity, thermal stability, response and recovery time of the sensor were measured and presented.

}, keywords = {(Ba0.87Sr0.13)TiO3 thick films, ammonia gas sensor, II2S gas sensor, selectivity, sensitivity}, issn = {0250-4707}, doi = {10.1007/s12034-007-0003-z}, author = {Jain, G. H. and Patil, L. A. and Patil, P. P. and Mulik, Uttam P. and Patil, K. R.} } @article { ISI:000243695000025, title = {Synthesis and characterization of mesoporous carbon through inexpensive mesoporous silica as template}, journal = {Microporous and Mesoporous Materials}, volume = {98}, number = {1-3}, year = {2007}, month = {JAN}, pages = {189-199}, publisher = {ELSEVIER SCIENCE BV}, type = {Article}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

Mesoporous silica materials have been synthesized through sol-gel reaction using inexpensive sodium silicate as source of silica and low cost hydroxy carboxylic acid compounds as templates/pore forming agents. The material measured surface area of 1014 m(2)/g, pore diameter of 65 angstrom and pore volume of 1.4 cc/g when parameters like time and temperature of synthesis along with mole ratio of TA/SiO(2) were optimized. Here TA stands for tartaric acid. Carbonization of sucrose inside the pores of above silica material at 900 degrees C followed by removal of silica framework using aqueous ethanoic solution of NaOH gave rise to mesoporous carbon material. The resulting materials were characterized by N(2)-sorption, FTIR spectroscopy, X-ray diffraction, transmission electron microscopy, X-ray photoelectron spectroscopy, thermal analysis and cyclic voltammetry. Three dimensional interconnecting wormhole channel arrangement of mesoporous silica template leads to mesoporous carbon replica with surface area of 1200 m(2)/g. X-ray photoelectron spectroscopic study (XPS) of the mesoporous carbon material shows the concentration of carbon atom in the range of 97-98\% with 1-2\% oxygen and negligible amount of silica. The electrochemical double layer capacitance behavior of carbon material with the specific capacitance value of 88.0 F/g at the scan rate of 1 mV/s appears to be promising. (C) 2006 Elsevier Inc. All rights reserved.

}, keywords = {Electrochemical properties, hydroxy carboxylic acid, mesoporous carbon, Mesoporous silica, sodium silicate}, issn = {1387-1811}, doi = {10.1016/j.micromeso.2006.09.003}, author = {Karandikar, Prashant R. and Patil, K. R. and Mitra, A. and Kakade, Bhalchandra A. and Chandwadkar, Asha J.} } @article { ISI:000262183900001, title = {Synthesis and characterization of high surface area CeO2-doped SnO2 nanomaterial}, journal = {Materials Chemistry and Physics}, volume = {112}, number = {3}, year = {2008}, month = {DEC}, pages = {719-722}, publisher = {ELSEVIER SCIENCE SA}, type = {Article}, address = {PO BOX 564, 1001 LAUSANNE, SWITZERLAND}, abstract = {

In the present investigation the synthesis and characterization of high surface area CeO2-doped SnO2 nanomaterial has been reported. The material was synthesized by coprecipitation process combined with surfactant incorporating method. The concentration level of Ce (III) additive was varied systematically from 1 to 11 wt.\%. After calcinations at500 degrees C,a high BET surface area of 40 m(2)/g was obtained for 7 wt.\% CeO2. The effect of variation of sintering temperature (600-800 degrees C/2h) on the particle size and surface area of a CeO2/SnO2 system was investigated. The material obtained was nanocrystalline, having particle size in the range of 10-16 nm. (C) 2008 Elsevier B.V. All rights reserved.

}, keywords = {CeO2:SnO2, Nanomaterials, sensors}, issn = {0254-0584}, doi = {10.1016/j.matchemphys.2008.06.022}, author = {Gambhire, A. B. and Lande, Machhindra K. and Kalokhe, S. B. and Shirsat, M. D. and Patil, K. R. and Gholap, Ramkrishna S. and Arbad, B. R.} } @article { ISI:000258026000010, title = {Synthesis and characterizations of NiTiO(3) nanoparticles prepared by the sol-gel process}, journal = {Philosophical Magazine Letters}, volume = {88}, number = {6}, year = {2008}, month = {MAR}, pages = {467-472}, publisher = {TAYLOR \& FRANCIS LTD}, type = {Article}, address = {4 PARK SQUARE, MILTON PARK, ABINGDON OX14 4RN, OXON, ENGLAND}, abstract = {

Nanocrystalline nickel titanate (NiTiO(3)) composite powders were prepared by the sol-gel process combined with a surfactant-assisted template method. The resulting powders were calcined at different temperatures ranging from 150 degrees C to 750 degrees C for 2 h in air. The results revealed that a pure hexagonal phase of NiTiO(3) could be obtained at the low temperature of 750 degrees C. The phase evolution of NiTiO(3) was investigated by X-ray diffraction patterns, Fourier-transform infrared spectroscopy, and X-ray photoelectron spectroscopy. Particle size and morphology were studied by transmission electron microscopy.

}, keywords = {Nanoparticles, nickel titanate, sol-gel process}, issn = {0950-0839}, doi = {10.1080/09500830802199709}, author = {Gambhire, A. B. and Lande, Machhindra K. and Kalokhe, S. B. and Mandale, A. B. and Patil, K. R. and Gholap, Ramkrishna S. and Arbad, B. R.} } @article { ISI:000263932600008, title = {Synthesis and characterization of high-surface-area Ag2O-doped SnO2 nanomaterial}, journal = {Philosophical Magazine Letters}, volume = {89}, number = {3}, year = {2009}, month = {MAR}, pages = {PII 909257359}, publisher = {TAYLOR \& FRANCIS LTD}, address = {4 PARK SQUARE, MILTON PARK, ABINGDON OX14 4RN, OXON, ENGLAND}, abstract = {

Nanosized tin dioxide-based powders containing silver and palladium oxides have been prepared by coprecipitation reaction. XRD, TEM, and XPS analysis were carried out for investigation of crystalline structure and surface morphology. The best reactive conditions were determined, such as the concentration of the reactants, pH value, surfactants, reaction temperature, and time. The material obtained is nanocrystalline, having a particle size in the range of 5.21-7.42 nm. Effect of doped-Ag2O on the crystal size of the nanoparticles and the influence of the presence of a second dopant (Pd) on the Ag2O/SnO2 matrix was discussed.

}, keywords = {Ag2O:SnO2, Nanomaterials, XPS}, issn = {0950-0839}, doi = {10.1080/09500830902758651}, author = {Gambhire, A. B. and Lande, Machhindra K. and Kalokhe, S. B. and Shirsat, M. D. and Patil, K. R. and Gholap, Ramkrishna S. and Arbad, B. R.} } @article { ISI:000281175500059, title = {Simple chemical co-precipitation/calcination route for the synthesis of simulated synroc-B and synroc-C powders}, journal = {Materials Chemistry and Physics}, volume = {123}, number = {2-3}, year = {2010}, month = {OCT}, pages = {695-699}, publisher = {ELSEVIER SCIENCE SA}, address = {PO BOX 564, 1001 LAUSANNE, SWITZERLAND}, abstract = {

A simple chemical co-precipitation/calcination route was developed for the synthesis of simulated synroc-B and synroc-C powders using mostly nitrate salts as starting chemicals and 20\% ammonia solution as precipitant. In this route, a mixed solution containing Al-nitrate, Ca-nitrate, Ba-nitrate, zirconyl nitrate and titanyl nitrate in the molar proportion required for synroc-B is added to dilute ammonia solution to precipitate these cations in the form of their hydroxides at room temperature by maintaining pH approximate to 10.5 during precipitation. Formation of a major fluorite phase with minor amounts of anatase, rutile and hollandite phases is observed in the powder obtained after calcination in air at 750 degrees C. Multiphase crystalline synroc-B matrix containing hollandite, perovskite, zirconolite, and rutile phases is obtained after sintering the heat treated powder in the form of pellets at 1230 degrees C for 4h in air. Similarly, pure synroc-C phases with 14 and 20\% simulated waste loadings were synthesized following the same synthesis protocol. These pre-treated powders with a high surface area of similar to 25 m(2) g(-1) gave sintered ceramics having density of similar to 90\% for 14 and 20\% waste loadings. (C) 2010 Elsevier B.V. All rights reserved.

}, keywords = {Ceramics, Chemical synthesis, Oxides, Sintering}, issn = {0254-0584}, doi = {10.1016/j.matchemphys.2010.05.039}, author = {Potdar, H. S. and Vijayanand, S. and Mohaideen, Kamal Khaja and Patil, K. R. and Joy, Pattayil Alias and Madhavan, R. Raja and Kutty, K. V. G. and Ambashta, Ritu D. and Wattal, P. K.} } @article { ISI:000291725100012, title = {Synthesis of Cu-ZnO and C-ZnO nanoneedle arrays on zinc foil by low temperature oxidation route: effect of buffer layers on growth, optical and field emission properties}, journal = {Applied Surface Science}, volume = {257}, number = {20}, year = {2011}, month = {AUG}, pages = {8366-8372}, publisher = {ELSEVIER SCIENCE BV}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

Different densities of ZnO nanoneedle films have been prepared by pre-coated zinc foils with thin layer of copper and carbon followed by thermal oxidation at 400 degrees C in air. The X-ray diffraction patterns show well defined peaks, which could be indexed to the wurtzite hexagonal phase of ZnO. The scanning electron microscope images clearly reveal formation of ZnO needles on the entire substrate surface. The X-ray photoelectron spectroscopy studies indicate that Cu and C ions are incorporated into the ZnO lattice. Photoluminescence studies evaluate different emission bands originated from different defect mechanism. From the field emission studies, the threshold field, required to draw emission current density of similar to 100 mu A/cm(2), is observed to be 2.25 V/mu m and 1.57 V/mu m for annealed zinc foil pre-coated with copper and carbon, respectively. The annealed film with copper layer exhibits good emission current stability at the pre-set value of similar to 100 mu A over a duration of 4 h. The results show that buffer layer is an important factor to control the growth rate, resulting in different density of ZnO needles, which leads to field emission properties. This method may have potential in fabrication of electron sources for high current density applications. (C) 2011 Elsevier B. V. All rights reserved.

}, keywords = {Buffer layer, Carbon, Copper, field emission, Nanoneedle, ZnO}, issn = {0169-4332}, doi = {10.1016/j.apsusc.2011.04.023}, author = {Jamali-Sheini, Farid and Patil, K. R. and Joag, Dilip S. and More, Mahendra A.} } @article { ISI:000309645000077, title = {Surface characterization of Au-ZnO nanowire films}, journal = {Ceramics International}, volume = {38}, number = {8}, year = {2012}, month = {DEC}, pages = {6665-6670}, publisher = {ELSEVIER SCI LTD}, address = {THE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, OXON, ENGLAND}, abstract = {

Au-ZnO nanowire films have been synthesized by annealing Zn foils coated with a thin layer of gold. An X-ray diffraction study found that the synthesized ZnO consists mainly of a hexagonal wurtzite structure along with a small amount of AuZn3 phase. Scanning electron images showed that the ZnO wires extend to several microns in length. X-ray photoelectron spectroscopy studies confirmed the oxidation states of Au and Zn. An asymmetric O ls peak indicates the presence of oxygen in an oxide layer and O H groups on the films surfaces. Photoluminescence (PL) spectra showed different visible peaks for pre-annealed films, while for annealed films an UV peak appeared. In addition, the PL analysis showed that the overall intensity of photoluminescence decreased significantly after the films were annealed. Raman spectroscopy results also indicated that the crystalline quality of the films improved with annealing. This could be attributed to a decrease in oxygen vacancies and/or absorption of O-H groups on the surface of ZnO film. The highly hydrophilic surface with a water contact angle of similar to 155 degrees was obtained after annealing in air. (c) 2012 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

}, keywords = {Au-ZnO, Highly hydrophilic, Nanowires, XPS}, issn = {0272-8842}, doi = {10.1016/j.ceramint.2012.05.054}, author = {Jamali-Sheini, Farid and Yousefi, Ramin and Patil, K. R.} } @article { ISI:000336351800043, title = {Solar photocatalytic degradation of methylene blue using doped TiO2 nanoparticles}, journal = {Solar Energy}, volume = {103}, year = {2014}, month = {MAY}, pages = {473-479}, publisher = {PERGAMON-ELSEVIER SCIENCE LTD}, address = {THE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, ENGLAND}, abstract = {

Doped-TiO2 nanoparticles (M:TiO2: Fe, Zn, Zr, Sb, Ce and nM:TiO2: B, C, N, P, S) with anatase structure were prepared by sol-gel method and characterized by X-ray diffraction (XRD), Transmission electron microscopy (TEM), X-ray photoelectron spectra (XPS), Brunauer-Teller method (BET), UV-Vis diffuses reflectance spectroscopy (DRS). Results revealed that the anatase structure is highly stable for all doped TiO2 prepared compounds with enhancement in the surface area. UV-Vis diffuse reflectance spectra showed that these dopants were responsible for narrowing the band gap of TiO2 and shifting its optical response from ultraviolet to visible-light region. The photocatalytic activities of these multi-doped TiO2 catalysts were investigated by degradation methylene blue in aqueous solution under solar-light illumination. The results showed an appreciable enhancement in the photoactivity of the C-doped TiO2 as compared to other multi-doped TiO2 because of the formation of Ti+3 species which prevent the recombination of electron-hole pairs in C-doped TiO2. (C) 2014 Elsevier Ltd. All rights reserved.

}, keywords = {Carbon, iron, Methylene blue, Solar photocatalysis}, issn = {0038-092X}, doi = {10.1016/j.solener.2014.02.043}, author = {Bhosale, R. R. and Pujari, S. R. and Muley, G. G. and Patil, S. H. and Patil, K. R. and Shaikh, M. F. and Gambhire, A. B.} } @article { ISI:000341464100041, title = {Surface studies on benzophenone doped PDMS microstructures fabricated using KrF excimer laser direct write lithography}, journal = {Applied Surface Science}, volume = {314}, year = {2014}, month = {SEP}, pages = {292-300}, publisher = {ELSEVIER SCIENCE BV}, address = {PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS}, abstract = {

his paper discusses microfabrication process for benzophenone doped polydimethylsiloxane (PDMS) using laser lithography. KrF excimer laser of 248 nm with 20 ns pulse width at repetition rate of 1 Hz was used for microfabrication of undoped and benzophenone doped PDMS. The doped-PDMS shows sensitivity below 365 nm, permitting processing under ambient light. The analysis of etch depth revealed that doped PDMS shows self developable sensitivity at lower fluence of similar to 250 mJ/cm(2). The unexposed and exposed surface was studied using Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), Raman spectroscopy and Scanning electron microscopy (SEM). Spectrocopic analysis indicated increase in C-O, C=O, Si-O-3 and Si-O-4 bonding at the expense of Si-C and Si-O-2 bonds of PDMS. In case of laser exposed doped-PDMS, removal of benzophenone from probe depth of spectroscopy was observed. Whereas the surface morphology of exposed and unexposed doped-PDMS was observed to be same, indicating clean development of PDMS micropattems. The present study indicates that addition of 3.0 wt.\% benzophenone in PDMS enhance self development sensitivity of PDMS. The self developable results on doped-PDMS are quite encouraging for its potential use in point of care Lab-On-Chip applications, for fabricating micropattems using direct write laser lithography technology.\ 

}, keywords = {Direct write laser lithography, Microfabrication, micropatterning, Poly(dimethylsiloxane) (PDMS)}, issn = {0169-4332}, doi = {10.1016/j.apsusc.2014.06.054}, author = {Kant, Madhushree Bute and Shinde, Shashikant D. and Bodas, Dhananjay S. and Patil, K. R. and Sathe, V. G. and Adhi, K. P. and Gosavi, S. W.} } @article { ISI:000338820600009, title = {Synthesis and luminescence of graphene-nano calcium sulphide composite}, journal = {Materials Chemistry and Physics}, volume = {147}, number = {1-2}, year = {2014}, month = {SEP}, pages = {57-64}, publisher = {ELSEVIER SCIENCE SA}, address = {PO BOX 564, 1001 LAUSANNE, SWITZERLAND}, abstract = {

Graphene-nanocrystalline calcium sulphide has been synthesized using in-situ reduction of calcium salt and graphene oxide. Graphene oxide was prepared using Hummer{\textquoteright}s method. Surface morphology and crystal structure of samples were observed by transmission electron microscopy (TEM) and X-Ray diffraction (XRD). Ultra thin graphene and graphene oxide sheets with size ranging between tens to several hundreds of square nanometers are observed in TEM images. The TEM micrographs of G-CaS show that CaS particles are embedded in graphene sheets and the average particle size of CaS particles in the composite is less than 50 nm. The reduction in the intensity of various functional groups in FTIR spectrum also confirms the formation of graphene. The UV-Visible spectra of CaS shows absorption peak at 220 nm with a small shoulder at 250 nm whereas in G-CaS 220 nm absorption peak has reduced intensity and the shoulder at 250 nm has now shifted to 270 nm due to modification in the defect structure of CaS by graphene. CaS and G-CaS shows photoluminescence emission at 470 nm (lambda(exc.) = 375 nm) and 440 nm (lambda(exc.) = 350 nm) respectively, however emission intensity of G-CaS is relatively lower than CaS. Although the emission intensity is found to be lower than CaS, addition of CaS to graphene in G-CaS complex has made graphene luminescent. XPS spectra also indicate reduction of various oxygen containing functional groups in highly reduced graphene oxide and G-CaS. (C) 2014 Elsevier B.V. All rights reserved.

}, keywords = {Luminescence, Nanostructures, powder diffraction, Precipitation}, issn = {0254-0584}, doi = {10.1016/j.matchemphys.2014.04.006}, author = {Sharma, Geeta and Patil, K. R. and Gosavi, S. W.} }